Name: self-adhesive modified bitumen waterproof membrane
Brand: Hongyuan
Availability: InStock

Product Details

HDPE self-adhesive modified bitumen waterproof membrane

Specification:

Materials	Crossing-laminated HDPE, high polymer adhesive, asphalt
Thickness	1.2mm; 1.5mm; 2.0mm
Width	1.0m
Length	20m/roll or customized
Surface	Apple green, other color need to be confirmed
Packing	woven bag with Hongyuan Logo on packing material

1. Introduction:

Hongyuan Waterproof has newly developed RAM-CL, a self-adhesive waterproof membrane made from cross laminated HDPE film, asphalt and high polymer adhesive. This product is featured by high property performance, cold application, excellent size stability, anti-UV and good tear resistance.

HDPE film used in this product is manufactured through cross-lamination processing, which enables the film elongation stable both in MD and TD, while no deformation is caused, black color more beautiful and with a better waterproofing effect.

Its polymer and cement-hydrate (silicate grid) form a cross interface structure, permanently sealed to cement base.

2. Cross Laminated HDPE Film

An ordinary film is single directional stretching film. Adhesive membrane with this film is easily wrinkled when temperature changes, even broken if heavy deformation.

The upper surface— black cross laminating HDPE film— is imported from Valéron Company in USA, the same supplier as the Grace. This film have a better tensile strength, tearing strength, anti-UV, and better waterproofing effect.

3. Advantages:

1) Cross laminated Valéron HDPE film, high tenacity, much better than ordinary PE film and PET membrane, perfectly combined with self-adhesive membrane to improve the waterproofing effect.

2) Excellent bonding force. Its polymer and cement-hydrate (silicate grid) form a cross interface structure, permanently sealed to cement base.

3) Anti-UV. Can be exposed to the sunshine around 3-6months, no deformation, ensure construction going on smoothly.

4) Good dimension stability. It will not shrivel due to great temperature variation when construction.

5) High impact resistance and puncture resistance.

6) Excellent anti-aging, weather resistance, resistant salt, acid and alkali.

7) Good adaptation to the climate.

4. Applicable Scope

1). applied in non-exposed roofs, underground waterproof projects, subways, tunnels and water channels. It is specially used in such constructions that no open fire is allowed to used.

2). Cement mortar is used to install RAM-CL onto base, while self-adhesive is recommended to use between membrane sheets.

5.Technical Data Sheet:

Technical standard: GB/T23457-2009 Type P

No.	Item				Index
					Type I	Type II
1	Tensile strength, N/50mm				≥210	≥220
2	Breaking elongation, %				≥160	≥200
3	Impermeability, (30 Mpa×120min)				No leakage
4	Tear resistance, N				≥25
5	Nail-rod tear strength, N				≥110
6	Low temperature flexibility, °C				No craking under -15 °C	No craking under -25 °C
7	Peel strength between sheets, N/mm			No treatment	≥1.0
				After heating
8	Heat resistance, (70°C×2h)				No slipping, flowing or dripping
9	Peel strength between sheet and cement mortar, N/mm			No treatment	≥2.0
				After heating	≥1.5
10	Peel strength after sheet and mortar soaked in water, N/mm				≥1.5
11	Size stability			Appearance	No slipping, flowing or dripping
				change rate, %	± 2.0
12	Oil permeability, pieces				≤2
13	Holding Power, min				≥15
14	Artificial weathering test		Appearance		No slipping, flowing or dripping
			Pull retention, %		≥80
			Low temperature flexibility		No craking under -13 °C
15		Heat aging test (70°C×168h)	Pull retention, %		≥90
			Breaking elongation retention, %		≥80
			Low temperature flexibility		No craking under -13 °C
16		Salt treatment^a (20% NaCl solution×30d )	Pull retention, %		≥90
			Elongation retention, %		≥80
			Low temperature flexibility		No craking under -13 °C
17		Alkali treatment^a (saturated NaOH solution×30d))	Pull retention, %		≥90
			Elongation retention, %		≥80
			Low temperature flexibility		No craking under -13 °C
18		Chlorideion penetration resistance, mg/cm²d			≤5.0x10^-3
Note: ^a for special designed projects that require these testing items

While the longitudinal and transverse value of Hongyuan RAM-CL is equal, which enables the sheet has stronger adhesion on fasteners than ordinary membrane.

Welcome to visit us.