Specifications

• Die cast LED Base
• Other processes: sand casting, investment casting, permanent mold casting, forging, stamping, welding, extrusion, CNC machining and assembling
• Other materials: cast iron, carbon steel, alloy steel, stainless steel, brass and zinc alloy
• Weight: 0.01 to 10000kg
• Used in metallurgy, automobile, aero, chemical, ship hardware, construction and other industries
• Surface treatment: sand blasting, painting, epoxy powder coating, anodizing, polishing, nickel plating, chrome plating
• Custom designs are accepted

•  

  • Die casting process description:

        Die casting is the process where molten metal is injected into a mold under high pressure in the range of 10 – 210 Mpa. This will result in a highly uniform casting with very good surface finish and exceptional dimensional accuracy. Usually this can either eliminate or greatly reduce the machining required to finish the part.

  • We can offer both the cold chamber process and the hot chamber process. In the cold chamber process the metal is ladled into the injection chamber for each shot. There is less exposure of the molten metal to the chamber walls and plunger. This is very useful for aluminum and copper alloys that would easily alloy with iron at elevated temperatures. The hot chamber process has the injection chamber which is connected to the die cavity permanently immersed in the molten metal. The hot chamber process is used for metals of low melting point and high fluidity such as tin and zinc.

    Minimum wall thickness and draft angles for die castings are as follows:
    Material                         Min. Thickness                         Min. draft angle
    Aluminum                       0.9 mm ( .035 in )                    0.5 degrees
    Zinc alloys                      0.6 mm ( .025 in )                    0.25 degrees
    Copper                           1.25 mm ( .050 in )                  0.7 degrees

    The materials that Donrex offers are alloys of aluminum, copper, zinc and magnesium. Zinc castings can be made with thinner wall thickness than aluminum due to high melt fluidity.

    We can produce parts from very small to about 30 kg (66 lbs ) for aluminum, 10 kg ( 22 lbs ) for magnesium, 50 kg ( 110 lbs ) for zinc and 5 kg ( 11 lbs ) for copper.

    

  Die casting machine

   

   

   

  CNC

   

  

   

   

  Machining workshop

   

  

   

  Packing