High Crushing Insulated Rotary Kiln Refractory Fire Brick Magnesia-Chrome Bricks

$High Crushing Insulated Rotary Kiln Refractory Fire Brick Magnesia-Chrome Bricks$

Magnesia Chrome Brick is made with sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate. The domestic so called magnesia –Chrome bricks .
The refractoriness of magnesia chrome bricks are more than 2000℃,and the refractory under load is a above 1550℃.Good steady volume in high temperature , the performance of meeting sudden cold and sudden hot is better than magnesia bricks. According to different requirements the contents of the Cr2O3 can be changed.

Magnesite Chrome Bricks Feature
1.High refractoriness
2.Good resistance to alkaline and slag
3.High refractoriness under load
4.Excellent slag resistance
5.Good thermal stability

Magnesite Chrome Bricks Application

The direct-bonded magnesia chrome brick is widely used in the cement rotary kilns, regenerator of the glass furnace, lining of the steel making electric furnace, permanent lining of the RH upper slot and bottom slot, barrel of VOD furnace, non-ferrous metallurgical furnace, lining of the limekilns, metal mixer etc.

Technical Data

High Crushing Insulated Rotary Kiln Refractory Fire Brick Magnesia-Chrome Bricks

$High Crushing Insulated Rotary Kiln Refractory Fire Brick Magnesia-Chrome Bricks$

Direct-Bonded Magnesia-Chrome Brick
Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.

Chemical & Physical Data

Brand	MgO %	Cr2O3 %	SiO2 %	A.P. %	BDg/cm3	CCS.MPa	R.U.L °C
DBMGe-8A	≥74	≥8	≤1.5	≤18	2.98	≥40	1660
DBMGe-8B	≥74	≥8	≤2.0	≤18	2.98	≥35	1600
DBMGe-12A	≥66	≥12	≤1.5	≤18	3.1	≥40	1660
DBMGe-12B	≥66	≥12	≤2.0	≤18	3.1	≥35	1600
DBMGe-16A	≥60	≥16	≤1.5	≤18	3.15	≥40	1660
DBMGe-16B	≥60	≥16	≤2.0	≤18	3.15	≥35	1600

Rebonded Magnesia-Chrome Brick

Main Application:It’s suitable for lining of the slag zone area of refining furnaces of VOD,SKF.

Chemical & Physical Data

Brand	MgO %	Cr2O3 %	SiO2 %	A.P. %	BDg/cm3	CCS.MPa	R.U.L °C
RBMG-16A	≥65	≥16	≤1.2	≤16	3.1	≥45	1750
RBMG-16B	≥60	≥16	≤1.6	≤16	3.1	≥40	1700
RBMG-20A	≥60	≥20	≤1.2	≤16	3.15	≥45	1750
RBMG-20B	≥60	≥20	≤1.2	≤16	3.15	≥40	1700

Semi-Rebonded Magnesia-Chrome Brick

Main Application:It’s widely used for every industrial furnaces of the metallurgical and building materials industry.

Chemical & Physical Data

Brand	MgO %	Cr2O3 %	SiO2 %	A.P. %	BDg/cm3	CCS.MPa	R.U.L °C
SBMG-16A	≥60	≥16	≤1.5	≤17	3.1	≥40	1750
SBMG-16B	≥60	≥16	≤1.8	≤17	3.1	≥35	1700
SBMG-20A	≥55	≥20	≤1.5	≤17	3.15	≥40	1750
SBMG-20B	≥55	≥20	≤1.8	≤17	3.15	≥35	1700