chrome magnesite refractory brick for rotary kiln lining
USD $600 - $1,000 /Ton
Min.Order:1 Ton
Zhengzhou Dengda Electric Melting Charging Co., Ltd.
chrome magnesite refractory brick for rotary kiln lining
Magnesia Chrome Brick is made with sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate. The domestic so called magnesia –Chrome bricks .
The refractoriness of magnesia chrome bricks are more than 2000℃,and the refractory under load is a above 1550℃.Good steady volume in high temperature , the performance of meeting sudden cold and sudden hot is better than magnesia bricks. According to different requirements the contents of the Cr2O3 can be changed.
Chrome Magnesite Bricks Feature
1.High refractoriness
2.Good resistance to alkaline and slag
3.High refractoriness under load
4.Excellent slag resistance
5.Good thermal stability
Chrome Magnesite Bricks Application
The direct-bonded magnesia chrome brick is widely used in the cement rotary kilns, regenerator of the glass furnace, lining of the steel making electric furnace, permanent lining of the RH upper slot and bottom slot, barrel of VOD furnace, non-ferrous metallurgical furnace, lining of the limekilns, metal mixer etc.
chrome magnesite refractory brick for rotary kiln lining
Direct-Bonded Magnesia-Chrome Brick
Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L °C |
DBMGe-8A | ≥74 | ≥8 | ≤1.5 | ≤18 | 2.98 | ≥40 | 1660 |
DBMGe-8B | ≥74 | ≥8 | ≤2.0 | ≤18 | 2.98 | ≥35 | 1600 |
DBMGe-12A | ≥66 | ≥12 | ≤1.5 | ≤18 | 3.1 | ≥40 | 1660 |
DBMGe-12B | ≥66 | ≥12 | ≤2.0 | ≤18 | 3.1 | ≥35 | 1600 |
DBMGe-16A | ≥60 | ≥16 | ≤1.5 | ≤18 | 3.15 | ≥40 | 1660 |
DBMGe-16B | ≥60 | ≥16 | ≤2.0 | ≤18 | 3.15 | ≥35 | 1600 |
Rebonded Magnesia-Chrome Brick
Main Application:It’s suitable for lining of the slag zone area of refining furnaces of VOD,SKF.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L °C |
RBMG-16A | ≥65 | ≥16 | ≤1.2 | ≤16 | 3.1 | ≥45 | 1750 |
RBMG-16B | ≥60 | ≥16 | ≤1.6 | ≤16 | 3.1 | ≥40 | 1700 |
RBMG-20A | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥45 | 1750 |
RBMG-20B | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥40 | 1700 |
Semi-Rebonded Magnesia-Chrome Brick
Main Application:It’s widely used for every industrial furnaces of the metallurgical and building materials industry.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L °C |
SBMG-16A | ≥60 | ≥16 | ≤1.5 | ≤17 | 3.1 | ≥40 | 1750 |
SBMG-16B | ≥60 | ≥16 | ≤1.8 | ≤17 | 3.1 | ≥35 | 1700 |
SBMG-20A | ≥55 | ≥20 | ≤1.5 | ≤17 | 3.15 | ≥40 | 1750 |
SBMG-20B | ≥55 | ≥20 | ≤1.8 | ≤17 | 3.15 | ≥35 | 1700 |
chrome magnesite refractory brick for rotary kiln lining
Chrome Magnesia Brick Packaging Details:
1.Fumigated pallet
2.A stable stack of bricks
3.Card edges
4.PET strap
5.Plastic wrap
6.Overall dimension:940*940*120m (Routine)