High Pure and Low Silica Corundum

Pure Corundum

Chrome Corundum

Brown Corundum

MA-99

MA-96

MCA-12

FZA

Al2O3 %

≥99

≥96

≥88

≥78

SiO2 %

≤0.2

≤14

Fe2O3 %

≤0.15

≤0.3

≤0.3

R2O %

≤0.15

Cr2O3 %

10-12

Apparent Porosity %

≤17

≤18

17-79

18

Bulk Density g/cm3

≥3.15

≥3.0

≥3.15

≥3.0

Cold Crushing Strength Mpa

≥100

≥70

80-100

98

Modulus of Rupture at High 
Temperature 1250°C Mpa

≥9.5

Refractoriness °C

≥1900

≥1850

0.2Mpa Refractoriness Under Load T0.6 °C 

≥1700

≥1680

≥1700

≥1680

Thermal Stability 1100°C
Water cycles

≥6

≥6

Reheat liner change 1600°C×3h %

≤±0.2

≤±0.3

0-0.2

1500°C×2h
0~0.2