Specifications

1.Chrome Brick used in severe corrosion areas of reinforcing fiberglass furnaces
2.Typical areas are throatsaamelter sidewalls,

Chrome Brick series

 

Item	High Cr2O3 Brick  TY-C94	High Cr2O3 Brick  TY-C93	Middle chrome Brick  TY-C85	Chrome- Corundum Brick  TY-CC60	Chrome- Corundum Brick  TY-CC30	Chrome- Corundum  TY-CC12
Cr2O3   %	94±1	≥93	≥86	≥60	≥30	≥12
TiO2  %	3.8±0.3	/	/	/	/	/
Al2O3   %		/	/	≤38	≤68	≥80
Fe2O3  %		/	/	≤0.2	≤0.2	≤0.5
Bulk density g/cm3	≥4.50	≥4.3	≥4.2	≥3.63	≥3.53	≥3.3
Apparent Porosity %	≤12	≤17	≤17	≤14	≤16	≤18
Cold Crushing Strength Mpa	≥250	≥100	≥100	≥130	≥130	≥120
Refractoriness under load (0.2Mpa,0.6%)		≥1680	≥1670	≥1700	≥1700	≥1700
Reheating linear change rate (1600°Cx3h)		±0.2	±0.2	±0.2	±0.2	±0.2

 

used in severe corrosion areas of reinforcing fiberglass furnaces and E-glass furnaces. Typical areas are throats, melter sidewalls, refiner sidewalls, bottom pavings, forehearths and back-up blocks

High-chrome bricks are mainly used in the key parts of the furnace for coal chemical industry, chemical industrial, alkali-free glass fiber and garbage incinerator, ect. Chromium-corundum bricks are mainly used for the lining of carbon soot furnace and copper smelting furnace, the skid rail molten pool of glass furnaces, and tapping platform of rolling mill furnace