Stress control heat shrinkable protection sleeve for 36kv joints/terminations
Negotiable /Roll
Min.Order:1 Roll
Dongguan Weishida Insulation Materials Co., Ltd.
Stress control heat shrinkable protection sleeve for 36kv joints/terminations
Features/Applications
HSC-360T is made from radiation cross-linked polyolefin material,The specially designed chemical formulation and carefully controlled manufacture technology effectively release the high electrical stress present at insulation termination of power cables terminations up to 36KV.
Minimum shrink temperature: 100°C
Minimum fully recovery temperature: 130°C
Technical data:
Property | Test Method | Typical Data |
Tensile strength | ASTM D 638 | ≥10MPa |
Elongation at break | ASTM D 638 | ≥300% |
Heat Shock (200°C/30mins) | ESI09-13 | No splitting, cracking dropping or flowing after 30 mins at 200°C |
Dielectric constant | IEC 250 | ≥45 |
Volume Resistance | IEC 93 | ≥109Ω .cm |
Low Temp Flexibility |
| No cracking after 4hrs at -20°C(max) |
Water absorption | ISO 62 | <1.0% |
Longitudinal shrinkage | -- | ±5% |
Eccentricity | ASTM S 2671 | <35% |
Normal size (mm) | As supplied (mm)
| After recovered (mm) | *Style
| Standard Length
| |
Inside diameter (min.) | Inside diameter (Max.) | Wall thickness (Nom.)
| |||
Continuous length tubing | |||||
47/18 | 47 | 18 | 2.5 | - | 30M/Spool |
Cut length tubing
| |||||
55/21 | 55 | 21 | 2.5 | 0 | 1000mm |
65/25 | 65 | 25 | 2.5 | 0 | 1000 mm |
75/30 | 75 | 30 | 2.5 | 0 | 1000 mm |
95/45 | 95 | 45 | 3.0 | 0 | 1000 mm |