black shrink tubing
Negotiable /Roll
Min.Order:1 Roll
Dongguan Weishida Insulation Materials Co., Ltd.
VERY LOW SHRINK TEMPERATURE , FLEXIBLE
HALOGEN FREE POLYOLEFIN TUBING
SHRINK RATIO 2:1
Features/Applications
H-2(LS) is manufactured with modified radiation cross-linked
Polyolefin. The specially designed halogen free formulation
makes the tubing very flexible and shrinking at lower
Temperature. Suitable for applications where heat sensitive
Compo and quick shrinkage is required.
Operating temperature: -45Celsius degree~+125Celsius degree
Minimum shrink temperature: 65Celsius degree
Minimum fully recovery temperature: 95Celsius degree
Meet: Sony SS-00259, RoHS
Standard color: Black
Technical Data:
Property | Test Method | Typical Data |
Tensile strength | ASTM D 2671 | 13MPa |
Elongation at break | ASTM D 2671 | 450% |
Tensile strength after aging at 158°C for 168 hrs | ASTM D 2671 | 11MPa |
Elongation after aging at 158°C for 168 hrs. | ASTM D 2671 | 300% |
Heat shock (250 °C/ 4 hrs.) | ASTM D 2671 | No cracking |
Cold bend test (-55°C / 4 hrs.) | ASTM D 2671 | No cracking |
Copper Corrosion | UL 224 | Pass |
Flammability | MVSS 302 | Pass |
Fluid resistance | 23°C for 24hrs ISO 37 tensile strength Elongation | 11MPa 200% |
Longitudinal shrinkage | UL 224 | 0±5% |
Product Dimensions (mm/inch)
Normal size | As supplied (mm) | After recovered (mm) | Standard length (m/spool) | |
(inch) | Inside diameter (Min.) | Inside diameter (Max.) | Wall thickness (Nom.) | |
1/16 | 1.6 | 0.8 | 0.50 | 200 |
3/64 | 2.4 | 1.2 | 0.50 | 200 |
1/8 | 3.2 | 1.6 | 0.50 | 200 |
3/16 | 4.8 | 2.4 | 0.50 | 200 |
1/4 | 6.4 | 3.2 | 0.60 | 100 |
5/16 | 8.0 | 4.0 | 0.60 | 100 |
3/8 | 9.5 | 4.8 | 0.60 | 100 |
1/2 | 12.7 | 6.4 | 0.60 | 50 |
5/8 | 16.0 | 8.0 | 0.60 | 50 |
3/4 | 19.1 | 9.5 | 0.80 | 50 |
1 | 25.4 | 12.7 | 0.90 | 50 |
1 1/4 | 31.8 | 15.9 | 0.90 | 50 |
1 1/2 | 38.1 | 19.1 | 1.00 | 50 |
2 | 50.8 | 25.4 | 1.10 | 50 |