three core conductive cable breakout protection sleeves
USD $0.2 - $1 /Piece
Min.Order:100 Pieces
Dongguan Weishida Insulation Materials Co., Ltd.
Three core conductive cable breakout protection sleeves
Features/Applications
Made from radiation crosslinked polyolefin. The electrically semi-conductive property of the breakout provides effective conductive screen and sealing protection to the cable terminations.
The breakout can be used to cable terminations up to 36KV.
Minimum shrink temperature: 110°C
Minimum fully recovery temperature: 130°C
Standard color: Black
Technical data:
Property | Test Method | Typical Data |
Operating temperature | IEC 216 | -55°C to +105°C |
Tensile strength | ASTM D 2671 | 12 MPa Min |
Tensile strength after thermal aging | ASTM D 2671 (120°C/168hrs) | 10 MPa Min |
Elongation at break | ASTM D 2671 | 250% Min |
Elongation at break after thermal aging | ASTM D 2671 (120°C/168hrs) | 200% Min |
Water absorption | ISO62 | 1% Max |
Volume resistance | IEC 93 | 104Ω.cm Max |
Order ref. Number | As supplied (mm) | After recovered (mm) | |||||||
D1 (Min.) | D2 (Min.) | D1 (Max.)
| D2 (Max.) | D3 (Nom.) | L(±10%)
| F(±10%)
| W1(±10%) | W2(±10%) | |
HCB320 60/24 | 60 | 25 | 24 | 8 | 29 | 183 | 45 | 3 | 2.5 |
HCB330 80/36 | 80 | 35 | 38 | 11 | 44 | 215 | 57 | 4 | 4 |
HCB340 110/48 | 110 | 46 | 50 | 17.5 | 56 | 250 | 65 | 4 | 4 |
HCB350 125/55 | 125 | 55 | 57 | 20 | 63 | 260 | 57 | 4 | 4 |
HCB360 140/68 | 140 | 62 | 70 | 26 | 76 | 280 | 70 | 4 | 4 |