Product Details

Product Description

Submerged welding liquid gas flux smd solder paste

TY-SJ101

SPECIFICATION: EN760 SA FB 1 65 AC H5

AWS A5.17/ 5.23 F6A0-EL8 F7A2-EM12K F7A4-EH14

APPLICATIONS

Horizontal welding of oil storage tanks, ships, bridges, pressure vessels, penstocks, boilers and structural steels.

CHARACTERISTICS:

TY-SJ101 is an agglomerated fluoride-basic type flux.

Metallurgical behavior: Slight silicon pick up. The behavior of manganese is neutral.

Grain size: 10 to 60 mesh.

Basicity: 1.8( BIIW).

TY-SJ101 assures excellent weldability, and the welding bead appearance is beautiful and the slag is easy to remove.

The diffusible hydrogen content in deposited metal is less than 5ml/100g, so it has very good toughness at low temperature, therefore, crack resistance is extremely high.

It is suitable for submerged arc twin- wire, tandom and multi- wire welding as well as for welding with the two- run technique.

Damp flux should be re-dried at 300-350℃ for 2 hours. Rust, grease and moisture on the weldment should be removed before welding.

Chemical Cmposition of SJ101( %)

SiO₂+TiO₂	CaF₂	AI₂O₃+MnO	CaO+MgO	S	P
15-20	15-20	25-30	25-30	≤0.05	≤0.05

Mechanical Properties of the ALL- WELD

WIRE	Yield Point (MPa)	Tensile Strength (MPa)	Elongation 5(%)	Charpy V Notch Impact Value(J)
WIRE	Yield Point (MPa)	Tensile Strength (MPa)	Elongation 5(%)	-20℃	-40℃
EM12K	≥400	490-600	≥22	≥50
EH14	≥400	500-650	≥22	≥70	≥50

SiO₂+TiO₂	Al₂O₃+MnO	CaO+MgO	CaF₂	S	P
25~35	50~60	5~10	5~10	≤0.05	≤0.05

Wires	Standard Models	_σs (Mpa)	_{_σb} (Mpa)	_δ5	Akv (J)
		≥400	≥420 ≥500	≥22% ≥22%	≥27 ≥27

Packaging & Shipping