Specifications

1.Superior mechanical and electric properties
2.Excellent resistance to oil, acids and alkalis

AG601 FIBERGLASS SLEEVING COATED

WITH ACRYLIC RESIN

 

 

Description

AG601 fiberglass sleeving is a Class 155°C electrical insulation,manufactured by impregnating and coating a finely braided fiberglass sleeving with a dielectric film of acrylic resin. AG601 sleeving isrecommended as a universal coated sleeving for all thermal requirements

 

Features

•Superior mechanical and electric properties

•High heat resistance (class F,155°C)

•Excellent compatibility with polyester,phenolic and epoxy resin.

•Excellent resistance to oil, acids and alkalis

 

Applications

widely used in fractional and integral horsepower

motors on leads and crossovers. Other uses exist in dry and oilfilled

transformers, relays of many types, radio and television circuits,

 

 

Available

Breakdown voltage

Grade A 7,000 Volts Min. Avg. 5,000 Volts Min. Indiv.

Grade B 4,000 Volts Min. Avg. 2,500 Volts Min. Indiv.

Grade C-1 2,500 volts Min. Avg. 1,500 Volts Min. Indiv.

Grade C-2 1,500 Volts Min. Avg. 800 Volts Min. Indiv.

 

Sizes

In continuous spooled lengths or cut lengths in 1000mm per piece

 

Colors

Black, yellow, white and natural.

Other colours are available on request

 

 

 

Technical Data

 

Inner Diameter     WallThickness
Size	Tolerance	Minimum	Maximun
1-3	±0.20	0.2	0.6
4-9	±0.30	0.3	0.7
10-16	±0.50	0.5	0.8

 

Performance Index (Table 2)

 

Performance                           Index
Breakdown Voltage(even)	4000
	2500
	1000
Bending at low temperature	No cracking or detachment of the coating shell be visible after 60 min at -15°C
Bending after heat treatment	No cracking or detachmant of the coating shell be visible after 48±1hr at 155°C±3°C
The other performances	Reference to GB7113-7117-86

 

Property	Requirements
Proof Voltage (not lower than)kv	under normal conditions		after dampening	after winding
	2.5 kv	4 kv	1.2 kv 2kv	1.5 kv 2.5kv
Coating stability	Temp 20o 5 the sleeving has been wound around the specified mandrel for 1 hour. The coating should not crack or appear detached.
	The sleeving is treated for 2hours at a temperature of 10 to 15o C below zero. Then has been wound around the specified mandrel immediately. Coating should not crack ar appear detached.
	The sleeving treated at a temperature of 130o 2o C for 24 hours and is wound around a specific mandrel at the room temperature of 20o 2o C The coating should not crack or appear detached.
Oil resistance	The sleeving dipped in transformer oil for 24 hours at a temperature of 105 2 C. The coating should not crack or appear detached. But the colour of the sleeving is allowed to grow darker.
Benzene resistance	The sleeving kept in methyl benzene at a normal atmospheric temperature for 4 hours. The coating should not be sticky or show delamination.