Specifications

1.Excellent dielectric strength and flexibility
2.High temperatures up to 200 degrees

Description

This product is comprised of a two-component liquid silicone rubber continuously applied to premium electrical grade braided fiberglass sleeving.

It offers superior coating adhesion to the fiberglass than extruded type products while retaining excellent flexibility and expandability over a wide range of temperatures (-55°C to +200°C).

 

Features

•Excellent dielectric strength and flexibility

•High temperatures up to 200°C

•Maximum flexibility and expandability

•VW-1 Chemical resistance

•Moisture resistance

•Cut-through resistance

•Radiation resistance

•Abrasion resistance

 

Applications

AC, DC motor lead protection, high current dry transformers and automotive under-the-hood wire protection.

 

Available

Sizes

Iin continuous spooled lengths or cut lengths in 1000mm per piece

Colors

Black, yellow, white and natural.

Other colours are available on request

 

Technical Data

 

Hardness	30 durometer, shore A
Tensile Strength	> 1000 psi
Elongation	> 600%
100% Modulus	300 psi
Tear strength	150 ppi
Compression set	> 8.0% (22 hrs @ 177°C)
Resistance to:
Ozone	excellent
Corona	excellent
Radiation	excellent
Sunlight	excellent
Fungus	excellent
Dielectric Grade	Min. Ave.	Min. Indiv.
	Breakdown
A	8000V	6000V
B	4000V	2500V
C-1	2500V	1000V
C-2	1500V	800V

 

 

Properties	Requirements	Results obtained
Prof voltage (kv)	1.5 kv to 12 kv
Self Extinguish	Flame must extinguish within 45 Secs	Self Extinguishment
Flexibility (Bending Test)	No crack should be observed when kept at temperature of 180oC for 72 hours.	No Crack Observed
Insulation Resistance	10x103M?	OK
Varnish Stability	No flow of varnish should be noticed when kept at temperature of 180oC for 72 hours.