WASPALOY
Waspaloy is an age hardening nickel base super alloy with useful strength at temperatures up to 1400-1600°F, and good oxidation resistance in gas turbine engine atmospheres up to 1600°F. The creep-rupture strength of Waspaloy is superior to that of alloy 718 at temperatures above 1150-1200°F. Short time hot tensile strength is inferior to alloy 718 at temperatures up to 1350°F.
Welding is difficult, and best performed on material in the solution annealed condition. Limit currents and the size of the fusion zone. Rapid cooling from welding is necessary to minimize aging stresses. Copper backup bars or water cooled fixtures are desirable. After welding, the fabrication should be solution treated, using rapid heating and cooling rates through the aging range. Follow anneal by stabilization and aging treatments.
A typical heat treatment is a solution heat teat at 1825°F for 2 hours, air cool. Stabilize heat treat at 1550°F for 4 hours, air cool. Precipitation heat treat at 1400°F for 16 hours, air cool.
Chemistry
| Cr | Ni | Mo | Co | Al | Ti | B | C | Zr | Fe | Mn | |||||||
MIN | 18.0 | -- | 3.50 | 12.00 | 1.20 | 2.75 | 0.003 | 0.02 | 0.02 | -- | -- | |||||||
MAX | 21.0 | Balance | 5.00 | 15.00 | 1.60 | 3.25 | 0.01 | 0.10 | 0.08 | 2.00 | 0.10 |
Si | P | S | Cu |
-- | -- | -- | -- |
0.15 | 0.015 | 0.015 | 0.10 |
Common trade names
WASPALOY
Features
Applications
Physical properties
Density: 0.296 lb/in3
Melting range: 2425 - 2475°F
Temperature, °F | 400 | 1000 | 1200 | 1400 | 1600 | 1800 |
Coefficient* of thermal expansion, | 7.0 | 7.8 | 8.1 | 8.4 | 8.9 | 9.7 |
Thermal conductivity | 7.3 | 10.4 | 11.6 | 12.7 | 13.9 | - |
Modulus of elasticity dynamic, | 30 | 27 | 26 | 24 | 23 | 21 |
* 70°F to indicated temperature.
Mechanical properties
Representative tensile properties heat treated, sheet
Temperature, °F | 70 | 1200 | 1400 | 1600 |
Ultimate tensile strength, ksi | 193 | 173 | 140 | 79 |
0.2% yield trength, ksi | 132 | 112 | 112 | 60 |
Elongation, % | 27 | 21 | 12 | 12 |
Hardness, Rockwell C | 34-40 | - | - | - |
Typical rupture strength, heat treated, sheet - stress to rupture at indicated time
Temperature, °F | 1200 | 1300 | 1400 | 1500 | 1600 |
100 hours, ksi | 92 | 75 | 53 | 32 | 18 |
1,000 hours, ksi | 80 | 57 | 35 | 19 | 10 |
More products for you to choose.
Production line
Testing Equipment
Certification
Packing picture:
Our market
Our advantages and services
a. Our advantage
We can provide high quality material, excellent design, precise manufacturing,complete specifications, considerate and integrity serivices.
We can provide all kinds of electric heating alloy material and elements, including customized products.
We can provide a complete solution for you.
OEM service can be provided.
b. Technical services we can provide:
Product selection
Process optimization
New product development
Contact information: