Specifications

Stainless steel flux cored welding wire AWS A5.22 E308LT1-1.
High porosity resistance.
All position welding.

 

Stainless steel flux cored welding wire AWS A5.22 E308LT1-1 welding for 18-8 low carbon stainless steel or the same type stainless steel. FCW Used to join base metals of similar composition, such as AISI 301, 303, 304, 305, 308, 308L, 347. By specifying low carbon in this alloy, it is possible to obtain resistance to inter granular corrosion due to carbide precipitate without the use of stabilizers such as Columbium or Titanium .This material is generally used with 100% Carbon Dioxide, or mixtures of Argon and Carbon Dioxide, typically 80%-20% mixture. Suggested wire stick out is 5/8"-3/4".

 

1. Chemical Composition of Deposited Metal (%)

Standard % :C≤0.08, Mn0.5-2.5, Si≤1.0, P≤0.04, S≤0.03, Cr 18.0-21.0, Ni9.0-11.0,

2.Mechanical Properties of Deposited Metal

Standard: Tensile Strength ≥550 Mpa, Elongation ≥35%

3. Available Diameter:

1.2MM /1.4MM/ 1.6MM

4. Shielding Gas:

100% CO2 or 80% Ar+20% CO2

5. Recommended Current (DC+) and Voltage Range

 

Precision layer winding, wrapped with volatile corrosion inhibitor paper, vaccum packed with aluminium foilbags, further packed in seaworthy corrugated carton.

15kgs/spool, 72cartons/pallet, 22pallets/20'container

 

We specialize in producing flux cored wire for more than 14years, we have ISO 9001:2000 certificate.We have 18 production lines with the capacity of 50,000tons per year. Our E71T-1 FCW performs very low spattering, high effective vertical welding, very stable arc and fast welding rate. The diffusible hydrogen content in the deposited metal reaches 3.5ml/100g, which significant avoid the cold cracking and porosity. We are the only FCW supplier in China has 3YH5 certification. We are also the biggest and best quality supplier in China for E71T-GS and E71T-11 self-shielding FCW products.