Melt mass-flow rate - MFR (230/2.16)

12

g/10 min

Moulding Shrinkage - SMp / SMn

1.4 / 1.3

%

Tensile Modulus of Elasticity

1500

MPa

Tensile Stress at Yield

35

MPa

Tensile Strain at Yield

9.0

%

Tensile Strain at Break

>50

%

Charpy Notched Impact Strength  (23°C)

2.5

kJ/m²

Ball Indentation Hardness - HB

75

N/mm²

Melting Temperature - DSC

163

C

Heat Deflection Temperature - HDT/A (1.8 MPa)

53

C

Heat Deflection Temperature - HDT/B ( 0.45 MPa)

85

Vicat Softening Temperature - VST/A 120 (10N)

154

Vicat Softening Temperature - VST/ B 120 (50N)

90

Density

0.905

g/cm³