PA6 GF 45% polyamide 6 PA plastic Nylon6 cf10% , gf45% , gf35 , gf45 granules PA6 GF30

Engineering Nylon: PA66, PA6 Plastic granules

For our Reinforced Nylon series, it avaliable for PA66 or PA6 with glass fiber range from 10% to 60%, for PA66 or PA6 with carbon fiber range from 10%-50%.

It has outstanding mechanical strength and good toughness;

It with high heat resistance performance, and good dimensional stability;

It has high flexibility performance in the low temperature: Minus 40 degrees Celsius condition;

For flame retardant propert, it reach V0 standard;

It has high CTI value , excellent electrical insulation, low smoke and low toxicity characteristics.

Advantages for PA6 gf:

Mechanical property, dimension stability, heat resistance and ageing resistance is obviously improved; Fatigue resistance is 2.5 times as the normal polyamide PA6.

Specifications:

1. 10%-50%cf filled

2. Antistatic
3. Good mechanical properties

4. Size stability

5. High toughness
6. Good abrasion property, weatherability

7. Reduce water absorption

8. Long-term work at higher temper

Product Description	Glass Fiber Reinforced PA6 Material
Product Grade	Injection Molding Grade
Appearance	Natural Pellet

Item	Typical Characteristic	Typical Characteristic	Testing Standard
Density	1.35g/cm3	1.39g/cm3	ASTM D-792
Glass Fiber	33%	45%	---
Molding Shrinkage	0.3%	0.25%	ASTM D-955
Tensile Strength	140MPa	150MPa	ASTM D-638
Elongation at break	3%	2.5%	ASTM D-638
Flexural Strength	205MPa	215MPa	ASTM D-790
Flexural Modulus	6900MPa	7600MPa	ASTM D-790
Heat Deflection Temperature	210℃	218℃	ASTM D-648
Flame Retardant	HB	HB