PVDF Resin with antioxidant properties
USD $47 - $47 /Kilogram
Min.Order:200 Kilograms
Quzhou Best Make Technology Co., Ltd.
1. Product Introduction
PVDF resin has weather resistance, light retention, color retention, chemical corrosion resistance, excellent post-processing, high temperature resistance, high cost performance, easy maintenance and high decoration.
2. Technical Parameter
Item | Test Method | Unit | Index |
Apparent Density | GB/T6373 | g/ml | 0.28~0.40 |
Water Content | GB/T6284 | % | ≤ 0.2 |
Purity | —— | % | ≥ 99.5 |
Scattered Fineness(30min) | GB/T1724 | μm | ≤ 30 |
Grinding Fineness(5min) | GB/T1724 | μm | ≤ 30 |
Stomer Viscosity | GB/T9269 | KU | 70±10 |
Melting Point | ASTM D3418 | ℃ | 156~165 |
Thermal Decomposition | TGA,1%wt.Loss Air | ℃ | ≥390 |
Melt Flow Rate | ASTM D1238 230°10kg | g/min | 0~3.0 |
3. Mark, Package, Storage & Transportation
3.1 Mark
The packaging barrel of this product shall be provided with firm and clear identification, indicating the company name, product name, batch number, brand (specification number), net content, etc.
3.2 Package
The product is packed in paper drums (lined with double-layer polyethylene plastic bags), and the net content of each barrel is (25 ± 0.2) kg; Each barrel shall be provided with product certificate, including company name, product name, batch number, brand (specification number), net content, production date, etc. If special packaging is required, the supplier and the buyer shall negotiate separately.
3.3 Storage
This product should be stored in a clean, cool and dry place to prevent rain, sunlight, moisture, dust and other impurities.
3.4 Transportation
This product is transported as non dangerous goods. Avoid moisture and violent vibration during transportation.
4. Main Application
PVDF resin mixed with acrylic resin and additives can form baking PVDF fluorocarbon coating with superior performance. The coating can be used for aluminum workpieces and aluminum curtain walls, such as plates, profiles, window frames and door frames, with a service life of more than 20 years. The base material must be pretreated before coating. Generally, the construction process of two coating and one drying and three coating and one drying is adopted. It is applicable to the surface of aluminum substrate such as building curtain wall, doors and windows, ceiling, roof and shop facade.