Product Details

H600

(E6-UM-60 )

DIN 8555 E 6-UM60 (35W)T

Description：

It deposits a self-hardening martensite structure. High hardness and good slag removal can be obtained. Suitable for pump impeller, cutter blade, agitator propeller, sugar crane hammers.

Diameters:

3.2mm, 4.0mm, 5.0mm

Typical Mechanical Properties：

As Welded	Interpass temp.150℃	Cont. Build Up
Vicker’s Hardness (HV)	620	590
Rockwell’s Hardness (HRC)	57	55
Shore’s Hardness (HS)	75	72

Typical Chemical Compositon:

C	Mn	Si	Cr	Mo
0.53	2.6	0.9	2.8	0.05

Welding Current (AC or DC+):

Dia:(mm)	3.2	4.0	5.0
Current/A	80-120	120-170	160-210

Note:

1. Rusty, water, oil and other impurity should be cleaned before welding.

2. Choose right welding parameter according to the requirements

3, Dry the electrodes at 80-120℃ for 1 hour or more

4, Preheat the weld piece and keep the inter-pass temp. above 200℃ to prevent cracking

5, Use low hydrogen electrode for buffer layer on difficult-to-weld steels