Spark Resistance Wire Ocr25Al5 Soft Bright Annealed Iron Chrome Aluminium K-D Alloy 0Cr21Al6Nb
Negotiable
Min.Order:1
Sino Erli Industrial And Trading Co., Ltd.
Ni80 Cr20Ni80 Cr20ni30 Nichrome Resistance Wire Tophet A Heat Resistant Wire
Nickel Chrome Steel Alloy Wire Spool Cr20Ni80 Nichrome Resistance Alloy Wire
Fecral cr23al5 cr25al5 resistance alloy wire for heater 145 fecr23al5 heating 0cr23al5
0cr25al5 Spiral Wire Resistance Heating Electrical Alloy 837
Toaster Element Wire Stove Resistance K-AF K-A1 Resistant For Heating
Heating High Resistance Wire Electric Heat Ocr21Al4 Electric Resistance Wire
FeCrAl high resistance and electric heating alloy
FeCrAl resistance & heating alloy with the characteristics of high resistance, low temperature coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature, as well as the lower price.
It is widely used in industrial electric furnace, household electrical appliance and far infrared ray device.
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main chemical composition (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC (μΩ·m) |
1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density (g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity (KJ/m·h·ºC) |
52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coefficient of lines expansion (α×10-6/ºC) |
15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point (approx.) (ºC) | 1450 | 1500 | 150 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area (%) | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Bending frequency (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous service time (Hours/ ºC) |
-- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Round wire: diameter 0.05mm-10.0mm
Flat wire: thickness 0.2mm-1.0mm, width 0.08mm-40.0mm