Fecral135 Wire Fecral Thermal Resistance Heating Alchrome DK
Negotiable
Min.Order:1
Sino Erli Industrial And Trading Co., Ltd.
0cr21al6nb Heating K-D Flat Wire/Ribbon Element Spring Wire Electrical Aluchrom 5
Cr20Ni80 Nichrome Wire In India Nikrothal 80 Alloy A Heating Spiral Elements
Kpx/knx type k thermocouple bright bare wire thermocouple cable
Fecral Element Wire 0Cr25Al5 Alloy 837 Industrial Electric Resistance Heating Wire
K Type Thermocouple Compensation Wire Thermocouple Wire Type T Roll
FeCrAl high resistance and electric heating alloy
FeCrAl resistance & heating alloy with the characteristics of high resistance, low temperature coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature, as well as the lower price.
It is widely used in industrial electric furnace, household electrical appliance and far infrared ray device.
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main chemical composition (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC (μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 |
1.23 |
1.45 |
1.53 |
|
Density (g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity (KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coefficient of lines expansion (α×10-6/ºC) |
15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point (approx.) (ºC) | 1450 | 1500 | 150 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 |
680-830 |
|
Elongation at rupture (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area (%) | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Bending frequency (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
continuous service time (Hours/ ºC) |
-- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Round wire: diameter 0.05mm-10.0mm
Flat wire: thickness 0.2mm-1.0mm, width 0.08mm-40.0mm