Cr21al6 Electric Resistance Alchrome DK Heating Resistance Wire Cr21Al4 Alloy For Heater
Negotiable
Min.Order:1
Sino Erli Industrial And Trading Co., Ltd.
2mm 3mm 5mm Thickness High Weather Resistant Alloy Fecral Stablohm 812 Resistance Wire
0cr21al4 fecral electric ribbon alloy sheet Heat Resistance Electric Wire
Fecralloy Fecral25/5 Alloy Fecral23-5 Wire Alferon 901 Cr23Al5Ti Strip Aluchrom 5 Resistance Wire
Type J Thermocouple Wire Color K Type Thermocouple Resistance Wire
Nichrome Electric Stove Wire Tophet A Resistence Nichrome 90 Vape Resistance Wire Strip
FeCrAl high resistance and electric heating alloy
FeCrAl resistance & heating alloy with the characteristics of high resistance, low temperature coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature, as well as the lower price.
It is widely used in industrial electric furnace, household electrical appliance and far infrared ray device.
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main chemical composition (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC (μΩ·m) |
1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density (g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity (KJ/m·h·ºC) |
52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coefficient of lines expansion (α×10-6/ºC) |
15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point (approx.) (ºC) | 1450 | 1500 | 150 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area (%) | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Bending frequency (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous service time (Hours/ ºC) |
-- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Round wire: diameter 0.05mm-10.0mm
Flat wire: thickness 0.2mm-1.0mm, width 0.08mm-40.0mm