NDT Series Digital Display  Drop Hammer Impact NDT Test Equipment

1.Application:

This machine is applicable for nil ductility transition temperature testing of ferrite steel. 

NDT temperature is the highest temperature when the standard specimen is broke 

according to the standard of ASTM E208-2006,GB/T 6803-1986. 

Also means the highest temperature of the crack steel occurred brittle fracture under 

dynamic loading yield stress.

 

2.Standards:

ASTM E208-2006,GB/T 6803-1986.

 

3.Main Technical Specifications:

 

Model	NDT-2000	NDT-3000	NDT-4000	NDT-6000
Max impact energy(J)	2000	3000	4000	6000
Min impact energy(J)	300	350	600	750
Hammer quality (Kg)	70	70	80	80
Main hammer body quality error	±1%
Impact height (mm)	750mm~3200
Impact speed (m/s)	3.8-7.6
Lifting hammer speed (m/min)	7
Height test resolution(mm)	0.1
Height test error(mm)	≤±10
Hammer blade hardness	HRC≥50
Hammer blade radius of curvature	R25mm
Bearing hardness	HRC58~62
Hammer blade center,Sample center and Support center deviation (mm)	≤±2.5
sample bearing span(mm)	P-1:305         P-2,P-3:100
Sample size(mm)(length×width×thickness)	P-1sample:(360±1)×(90±2)×(25±2.5) P-2 sample:(130±1)×(50±1)×(20±1) P-3 sample:(130±1)×(50±1)×(16±0.5)
(optional)high temperature device	0°C -- 100°C,low temperature 0~-80°C

 

4. Features:

Composed by framework, ascension, hammer body, the anvil block, safety protection 

and control systems.Through adjusting the number of weight thallium and impact height 

to adjust the impact energy. With anti secondary attack, automatic send sample function.

Specimen alignment is accurate and fast, energy range stepless adjustable, with energy 

automatic display function.

 

 Digital Display   Drop Hammer Impact Test Machine 

 