chemical tempered glass (also known as ionic exchange enhancement glass):

through the ionic exchange, the alkaline metal ion of glass surface is placed by other alkaline metal ion in salt melted, enhancing its mechanical strength.

product characteristics:

higher strength: it is 9-15 times higher of ordinary glass, its maximum destruct-resistance pressis600 mpa.

its strength may be adjusted to the request of the customer.

its surface is smoothness, does not distort, no spot.

absolutely no self-detonate problem.

ultra-thin glass, various kinds of abnormal-shaped glass also may be processed easily.

when it is broken, its fragments stay non-granulated.

after chemical tempered, it can be cut, coated, sandwiched glue etc.

products usage:

windscreen of airplane, train, and high quality car & boat.

 high grade construction glass.

opticalinstrumental cover.

surface board of copier, scanner and domestic electrical appliance

cup, fish tank and any other glass products etc.

product specification:

:3600mm×2400 mm max. size: 3600mm×2400mm

min. size: unlimited

thickness: unlimited

figure: unlimited

:manufacturing dimension and figure:

jc/t 977-2005

nation industry standard: jc/t 977-2005

table-1: surface stress of chemical tempered glass

sort	surface stress p (mpa)
i (grade-i)	300
ii (grade-ii)	400
iii (grade-iii)	p>600

 

table-2:impact-resistance ofchemical tempered glass
glass thickness (mm)	impact height (m)	steel ball weight (g)	pattern size (mm)
<2	1	227	300×300
2	2	227	300×300
3—5	3	227	300×300