Hot rolled JIS G4105 SCM440 Alloy Steel round bars
USD $600 - $1,200 /Ton
Min.Order:5 Tons
Liaocheng Kuncheng Pipe Co., Ltd.
SCM440 alloy steel is a chromium molybdenum alloy steel specification widely used in general purpose high tensile steel for components, like axles, shafts, bolts, gears and other applications. Similar to alloy grade SCM435 chrome moly alloy steel but with a slightly higher carbon content. The higher carbon content of SCM440 steel gives greater strength and heat treatment capabilities in comparison to SCM435 alloy steels, however it does have inferior weldability characteristics.
1. Supply Range for alloy SCM440 steel bar
SCM440 Steel Round Bar: diameter 8mm-3000mm
2. Common SCM440 Steel Specifications
Country | USA | German | British | Japan | China | Australia |
Standard | ASTM A29 | DIN 17200 | BS 970 | JIS G4105 | GB/T 3077 | AS 1444 |
Grades | 4140 | 1.7225/ 42crmo4 | 42CrMo4 | SCM440 | 42CrMo | 4140 |
3. SCM440 Steel Bar Chemical Composition
Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
ASTM A29 | 4140 | 0.38-0.43 | 0.75-1.00 | 0.035 | 0.040 | 0.15-0.35 | – | 0.8-1.10 | 0.15-0.25 |
EN 10250 | 42CrMo4/ 1.7224 | 0.38-0.45 | 0.6-0.9 | 0.035 | 0.035 | 0.4 | – | 0.9-1.2 | 0.15-0.30 |
JIS G4105 | SCM440 | 0.38-0.43 | 0.60-0.85 | 0.03 | 0.03 | 0.15-0.35 | – | 0.9-1.2 | 0.15-0.30 |
4. Mechanical Properties of Alloy SCM440 Steel Bar
Properties | Metric | Imperial |
Tensile strength | 655 MPa | 95000 psi |
Yield strength | 415 MPa | 60200 psi |
Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
Elastic modulus | 190-210 GPa | 27557-30458 ksi |
Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
Elongation at break (in 50 mm) | 25.70% | 25.70% |
Hardness, Brinell | 197 | 197 |
Hardness, Knoop (converted from Brinell hardness) | 219 | 219 |
Hardness, Rockwell B (converted from Brinell hardness) | 92 | 92 |
Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only) | 13 | 13 |
Hardness, Vickers (converted from Brinell hardness) | 207 | 207 |
Machinability (based on AISI 1212 as 100 machinability) | 65 | 65 |
Hot rolled scm440 alloy steel round bar