Property	Specification Requirement	Test Method	Typical Value
Tensile strength(Room temp.)	Min.10.4Mpa	UL224	17.2Mpa
Elongation at break(Room temp.)	Min.200%	UL224	280%
Tensile strength after aging(158℃ 168hrs)	Min.7.3Mpa	UL224	11.5Mpa
Elongation after aging(158℃ 168hrs)	Min.100%	UL224	200%
Voltage withstand(Uh-aged)	Withstand 2.5kv for 1 minute and breakdown	UL224	pass
Voltage withstand(Aged)	Withstand at least half of un-aged breakdown  voltage for 1 minute and breakdown	UL224	pass
Copper corrosion(158℃ 168hrs)	No corrosion of bare copper	UL224	No sign of deg.
Copper stabiity(158℃ 168hrs)	No sign of degradation (min.elongation 100%)	UL224	pass
Cold blend(-30℃ 1hrs)	No crack	UL224	pass
Maximum secant modulus(2%)	173Mpa	UL224	pass
Volume resistivity	Min.1014Ω.m	UL224	pass
Heat shock(250℃ 4hrs)	No crack	ASTM D2671	pass
Dielectric strength	>15.8kv/mm	ASTM D2671	>25kv/m