Stainless steel sintered porous material

Stainless steel sintered porous material is stainless steel 304, 304L, 316, 316L powder as the raw material, after screening, molding, sintering microporous material.

1.Features of stainless steel sintered porous materials

Stainless steel sintered porous material has excellent corrosion resistance, oxidation resistance, wear-resistance, and mechanical properties.

Material	Filter Rating	Porosity	Penetrability	Working pressure	Operating temperature	Shape	specific surface area
Stainless steel powder	0.5um-70um	30-45%	3-1300M³/M²hKPa	3.0MPa	600℃	Round Disc、Sheet、Tube、Round Bar、cap.	10-40cm²/cm³

2.Manufacture Standard

GB/T 6886-2008 Sintered stainless steel filter elements

3.Specification of SS304/SS304L/SS316/SS316L sintered porous materials

Production	(Diameter)Length	(Diameter)Width	Thickness	Customized
Sintered porous round discs	φ5-φ300mm	φ5-φ300mm	0.5-10mm	Yes
Sintered porous sheets	5-300mm	5-300mm	0.5-10mm	Yes
Sintered porous tubes	100-1200mm	φ20-φ200mm	1-10mm	Yes
Sintered porous cartridge	100-1200mm	φ20-φ200mm	1-10mm	Yes

4.Properties of stainless steel sintered porous materials

1) High-temperature resistance, in normal use under 500 ℃.

2) High mechanical strength, good plasticity, can be machined.

3) Corrosion resistance, oxidation resistance, can be used in nitric acid, sulfuric acid, dilute hydrochloric acid (5%), acetic acid, liquid hydrogen, liquid nitrogen environment.

4) Good molding process, according to customer drawings for processing a molding.

5) High filtration precision and good purification effect.

6) The pores are uniform, the internal structure is stable, and no particles fall off.

7) Good air permeability, easy to back blow cleaning, can be used repeatedly online regeneration.

8) Wear resistance and impact resistance, good mechanical properties.

5.Application of stainless steel sintered porous materials

According to its physical and structural characteristics, stainless steel sintered porous materials are mostly used in the fields of noise elimination, filtration and separation, fluid distribution, flow-limiting, capillary core, and so on.

1) The chemical raw material production process in addition to impurity filtration, material decarburization filtration, and fine filtration.

2) Ultrafiltration, RO, EDI system security filtration in water treatment.

3) The food and beverage industry finished product clarification filtration.

4) Filtration and recovery of the precious metal catalysts in the petrochemical industry.

5) Precision filtration of liquid raw materials, products, and pharmaceutical intermediates in the chemical industry.

6) Reverse osmosis security filtration in the field of water injection filtration.

7) Gas purification of steam, compressed air deoiling purification.

8) Medium purification and flow limitation for pneumatic components, lubricants, fuels, and hydraulic pressure systems.

9) Chemical dye industry of high - temperature decarburization.

6. Stainless steel sintered porous material allows for the use of the environment

Nitric acid, sulfuric acid, acetic acid, oxalic acid, phosphoric acid, 5% hydrochloric acid, molten sodium, liquid hydrogen, liquid nitrogen, hydrogen sulfide, acetylene, hydrogen, carbon dioxide gas, water vapor, etc.

Precautions for the use of stainless steel sintered porous materials：

1) During installation, disassembly, and clean avoid scratches, collisions, and falls on hard objects.

2) When using, the filtrate is filtered from the outside in to avoid the reverse direction.

3) Avoid instant pressurization when the filter element works.

4) When the filtration efficiency is less than 50%, the filter element should be cleaned in time.

5) When cleaning the filter element, first back blowing with pure gas, back blowing pressure is 1.5 times the working pressure, each time for 3-5 seconds, and 4-6 times, then backwash with clean liquid for 3-5 minutes, repeat 2-3 times.

6) If the filter element is not good after online back blowing and backwashing, it should be removed and cleaned in time.

7.Method for cleaning stainless steel sintered porous materials

1) The decarbonization filter elements in the pharmaceutical and chemical industries are mainly back blown and back washed, and the ultrasonic cleaning is the best.

2) The filter elements of the water industry are mainly rinsed with a 5% concentration of nitric acid.

3) According to the chemical properties of the filtered impurities, the filter elements of the original liquid shall be respectively soaked in pickling (5% nitric acid) or alkaline washing (3-5% sodium hydroxide) and then washed with ultrasonic cleaning.