Uns S35000 AISI 633 AMS5548 AMS5745 Stainless Steel Rod

350 is a stainless steel with chromium nickel molybdenum added and can be hardened by martensitic transformation and precipitation hardening. Depending on the heat treatment, the 350 may be an austenitic structure with the best molding properties; it can also be a martensitic structure with martensitic stainless steel strength. The alloy usually contains 5-10% delta ferrite. Its corrosion resistance is close to other chrome-nickel austenitic stainless steels.
350 alloy can be used for turbine compressor parts, such as blades, brake discs, rotors, shafts, etc. at room temperature and medium temperature need to withstand high strength parts.
 
chemical component%

350 alloy corrosion resistance is better than other hardenable martensitic stainless steel. In the normal environment and a variety of mild chemical environment, 350 alloy showed good corrosion resistance. The material in the repeated aging state is susceptible to intergranular corrosion because of the occurrence of chromium carbide precipitation. However, if the material by the following method to do the hardening treatment, can be better tolerated intergranular corrosion.
The stress corrosion resistance of the 350 alloy was increased by heating to 1010-1066 ° C, rapidly cooling to room temperature, cooling for 3 hours at -73 ° C and then reheating to 927-954 ° C for 90 minutes / Inch thickness, quickly cooled to room temperature, cooled at -73 ° C for 3 hours, and then tempered at 538 ° C for 3 hours.
In order to achieve the best corrosion resistance, the surface of the material shall not be skin, can not have lubricants, foreign objects and so on. After processing, parts should be thoroughly cleaned and passivated.
 
Physical properties
 
Specific gravity: annealed state -7.92; low temperature cooling, 454 ° C tempering state -7.81
Density: annealing state -0.2860 lb / in3; tempering state -0.2820lb / in3
Melting distance of 2500-2550 ° F 

Pictures of stainless steel bar :