*Similar Grade
GB | JIS | KS | Trademark | UNS | DIN EN/DIN | W-Nr. | NF | ГОСТ | BS EN/BS |
GH3600 NS3105 NS315 | NCF 600B NCF 1B | NCF 600 | Inconel 600 | N06600 | NiCr15Fe8 | 2.4816 | NiCr15Fe8 | - | NiCr15Fe8 NA14 |
*Product Forms
Pipe, Tube, Sheet, Strip, Plate, Round Bar, Flat Bar, Forgings, Hexagon, Wire
*Brief
Inconel 600 is a nickel-chromium alloy with good oxidation resistance at higher temperatures, with good resistance in carburizing and chloride containing environments. Alloy 600 is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of 1093℃. The high nickel content of the alloy enables it to retain considerable resistance under reducing conditions and makes it resistant to corrosion by a number of organic and inorganic compounds. The nickel content gives it excellent resistance to chloride-ion stress-corrosion cracking and also provides excellent resistance to alkaline solutions. Its chromium content gives the alloy resistance to sulfur compounds and various oxidizing environments. The chromium content of the alloy makes it superior to commercially pure nickel under oxidizing conditions. In strong oxidizing solutions like hot, concentrated nitric acid, 600 has poor resistance. Alloy 600 is relatively un-attacked by the majority of neutral and alkaline salt solutions and is used in some caustic environments. The alloy resists steam and mixtures of steam, air and carbon dioxide. Alloy 600 is non-magnetic, has excellent mechanical properties and a combination of high strength and good workability and is readily weldable. Inconel 600 exhibits cold forming characteristics normally associated with chromium-nickel stainless steels. Typical corrosion applications include titanium dioxide production (chloride route), perchlorethylene syntheses, vinyl chloride monomer (VCM), and magnesium chloride. Alloy 600 is used in chemical and food processing, heat treating, phenol condensers, soap manufacture, vegetable and fatty acid vessels and many more.
*Chemical Composition,%
% | Ni | Cr | Fe | C | Mn | Si | P | S | Cu |
Min | 72.0 | 14.0 | 6.0 | ||||||
Max | 17.0 | 10.0 | 0.15 | 1.0 | 0.50 | 0.02 | 0.015 | 0.5 |
*Typical Physical & Mechanical Property(Solution Annealed)
Density | Melting point | Tensile strength, MPa | Yield strength, MPa | Elongation,% |
8.47g/cm3 | 1354-1413℃ | 550-690 | 170-345 | 35-55 |
*Specification
Rod, Bar, Wire, Forgings | ASTM B166/ASME SB166, ASTM B564/ASME SB564, DIN 17752/17753/17754, ISO 9723/9724/9725 DIN 17752, ISO 9723 |
Plate, Sheet, Strip | ASTM B168/ASME SB168, ASTM B906/ASME SB906, DIN 17750, ISO 6208 |
Pipe, Tube | ASTM B167/ASME SB167, ASTM B163/ASME SB163, ASTM B516/ASME SB516, ASTM B517/ASME SB517, ASTM B751/ASME SB751, ASTM B775/ASME SB775, ASTM B829/ASME SB829, DIN 17751, ISO 6207 |
Others | ASTM B366/ASME SB366, DIN17742, ISO4955A |
*Feature
1. Virtually immune to chloride ion stress corrosion cracking
2. Good caustic corrosion resistance
3. Resistant to dry Cl2 to about 1000°F(540℃)
4. Oxidation resistance to 2000°F(1094℃)
5. Carburization resistance
*Application
1. Barge and tank truck liners
2. Carburizing atmospheres
3. Ethylene dichloride crackers
4. Furnace trays, mufflers, hangers
5. Gasoline stabilizer production
6. MgCl2 evaporates
7. Phenol condensers
8. Soap manufacture
9. Titanium dioxide
10. Vegetable and fatty acid vessels