Nickel sheets, Nickel plate, Nickel foil
Grade: N2.N4,N5,N6,N7,Ncu30,Ncu40
Standard: ASTM B160,ASTM B161,ASTM B162
Size: 1. T0.3mm--4.0mm*W300-3000mm*L500-4500mm(Cold rolling)
2. T4.1mm--50.0mm*W300-3000mm*L500-4000mm(Hot rolling)
Technique: Cold rolled/Hot rolled
Inspection equipment: Nondestructive Tester; UT Testing Detector; Tensile Tester
Digital Ultrasonic Detector; Infrared Tester; HV Hardness Tester
Application: 1.Chemical processing, medical instruments etc.
2.Indusrty,Navigation,Smelting,Chemical plants, and so on.
Standard seaworthy package

Delivery: 25days after received the 30% deposit.
Nominal composition:

Alloy	Ni%	Mn%	Fe%	Si%	Cu%	C%	Ti%
Nickel 200	Min 99.2	Max 0.30	Max 0.2	Max 0.10	Max 0.20	Max 0.10	Max 0.10
Nickel 201	Min 99.2	Max 0.30	Max 0.2	Max 0.10	Max 0.20	Max 0.02	Max 0.10

Physical feature:

Density in 700F 8.90 g/cm3; 0.322 ib./cu.in
Linear expansion coefficient (Inch/Inch/0C) 20-100ºC 0.000014 20-200ºC 0.000014
Linear expansion coefficient (Inch/Inch/0C) 0.000015 20-700ºC 0.000016
Youngs modulus of elasticity,E,PSI×10-6 30.1
Conductivity 22.6% IACS
Specific resistance in200C microhm.cm:7.63 ohms/cir.mil./ft.:45.9
Thermometric conductivity cal./cm.2sec.0C/cm.at700C:cal./cm.2sec.0C/cm.at700C:0.206 BTU/ft.2/hr./0F/ft.at 1580C:49.9
Temperature coefficient of resistance 200-1000C/0C 0.0058 200-5000C/0C 0.0074 200-8000C/0C 0.0060
Atomic number 28 Atomic weight 58.1
Atomic radius(A) 1.25 Crystal structuref.c.c
Crystal constant(A) 3.52 Melting point 1.4530C; 2.6470F Boiling point 2.7300C;4.9500F
Latent heat of fusion 73.8cal./g Specific heat at 200C-BTU/ib./0F 0.105
Interelectrode potential 0.25volts Velocity of sound 16.300ft./sec.;4.973m/sec.
Poisson ratio 0.31 Thermal neutron cross section ( target ) absorption:4.6 Scatter:17.5

Magnetism:

Curie temperature 3530C; 6650F Initial permeability 130
Maximum permeability 124 Saturation induction(B) 6050
Remnant induction(B) 3250 Diamagnetism(H) 3.0