Product Details

GBB-R melt flow index tester

Melt Flow Index Testing Equipment

Function and usage

To test the melt flow rate (MFR, unit: g/10min) of thermoplastic material in high temperature, such as polyethylene, polystyrene, polypropylene, ABS resin, acetal resin, polycarbonate, nylon, and fluoroplastic etc, widely used in industries of plastic material, plastic products, petroleum, chemicals, research institute, inspection agency and so on.

Standards:

GB/T9643, GB/T3682, JB/T5456, ISO1133

Working principle:
GBB-R Melt Flow Indexer makes the test material reach molten state at a prescribed temperature in the high-temperature furnace. Such melt test material goes through a small hole of specific diameter at a normative load, subjected to extrusion test. In the production of plastics, MFI is usually used to indicate the fluidity, viscosity and other physical properties of polymers. Melt flow rate is expressed in the weight or volume of polymer per 10 minutes of the test or the average weight of each extruded material.

Applications:

Thermoplastic materials such as polyethylene, polystyrene, polypropylene, ABS resin, polycarbonate, nylon, fluoroplastic and etc.

Specifications:

Test method	weight method (MFR), volume method (MVR)
Test range for weight method	0~200g
Test range for volume method	0~80cm3
Test accuracy for weight method	0.01g
Auto time count	0.1~999.9s
Temperature range	room temperature ~ 450 ℃
Temperature accuracy	± 0.1 ℃
Temperature fluctuation	≤ 0.5 ℃
Displacement accuracy	0.1mm
Temperature recovery time after adding sample	≤ 4min
Cutting mode	automatic timed cutting (0.1 ~ 999s), manual cutting
Die port inside diameter	Φ2.095 ± 0.005mm
Sample cylinder inside diameter	Φ9.550 ± 0.025mm
Standard load	3.187~211.82N, eight grades, accuracy ≤ ±0.5%
Instrument size	450x200x550mm