Product formation:

The composition of the matrix resin, catalyst, carbon forming agent and foaming agent

This product is fireproof coating for steel ,this paint is made of special resin ,fire retardant materials ,titanium dioxide and other materials. It can prevent the heat transfer of the flame,and make time for fire extinction so as to decrease hazard loss.

Product features:

 Protecting the steel structure from deformation, beam bending ,because it lost the carrying capacity over temperature of 450-650℃ . If no paint, it will damage and can not continue to use.

 Application:

1.Please do the necessary substrate treatment such as derusting ,dedusting and degreasing, and then apply the anti-corrosive primer paint such as zinc rich primer paint or epoxy mio paint.

2.Make sure the paint is fully mixed before use.

3.Please do not use this product when moisture content RH>90 or T<5℃.

4.No fire or eletric welding work allowed before the coating is hard dry.

5.Diluent rate:0%-10%.

Technical Data:

Color and appearance of paint film                       Colors and smooth film

Drying time, drying (150 degrees C), H                         1

Adhesion (zoned method), class                                   ≤1

Impact strength, kg, cm                                                 ≥50

Flexibility, mm                                                                10

Thickness of dry film, μm                                               30-60

Hardness (swing rod method)                                        ≥0.4 

Covering powder, g/㎡                                                   ≤ 85

Heat resistance                                                             Good

Using:

Widely used for fire protecting and decorating the power plants, modern buildings and large area bare or hidden steel structure