1.Material:steel

2.Place of Origin: Jiangsu, China (Mainland)

3.High hardness: The surface hardness can be 57- 67HRC: the 

volumetric hardness can be 56-64HRC, and the distribution of 

hardness gradient is even.

4.Low breakage rate: The  peel  resistance  and  breakage

 resistance  are  more than 10times than the peel resistance

 and breakage  resistance of traditional steel balls. When the

 ball impacts more than 10000 times, the actual breakage rate

 is less than 1% nearly no breakage.

5.High impact toughness

6.Good wear resistance

7.Dia:20mm-125mm

8.Appearance: Roundness, No crack and scars on the surface

9.Metallurgical Structure: microstructure is uniform from edge to 

center