Model No.:AL-6061
Product Origin:China
Brand Name:
Price Terms:FOB Shanghai
Payment Terms:L/C at sight or T/T
Certification:ISO9001, SGS
Description:Table 1, typical composition of aluminum alloy 6061 -T6 Component amount (weight %) Aluminum balance Magnesium: 0.8-1.2 Silicon: 0.4-0.8 Iron: max. 0.7 Copper: 0.15-0.40 Zinc: max. 0.25 Titanium: max. 0.15 Manganese: max. 0.15 Chromium: 0.04-0.35 Others: 0.05 Key properties: Typical properties of aluminum alloy 6061 include: Medium to high strength Good toughness Good surface finish Excellent corrosion resistance to atmospheric conditions Good corrosion resistance to sea water Can be anodized Good weld ability Good workability Widely available Note: property data is provided below, but should be used a guide only. As data may vary between manufacturers, you should consult your supplier for more exact figures Physical properties: Density: 2.7g/cm³ Melting point: approx. 580°C Modulus of elasticity: 70-80GPa Poisson ratio: 0.33 Mechanical properties: Temper ultimate tensile strength (MPa) 0.2% proof stress (MPa), brinell hardness (500kg load, 10mm ball), elongation 50mm dia. (%) 0, 110-152, 65-110, 30-33, 14-16 T1: 180, 95-96, 16 T4: 179min, 110min T6: 260-310, 240-276, 95-97, 9-13 Thermal properties: Co-efficient of thermal expansion (20-100°C): 23.5 x 10-6m/m °C Thermal conductivity: 173W/m.K Electrical properties: Electrical resistivity: 3.7- 4.0 x 10-6 Omega.cm Typical heat treatment/temper states Treatment definition F as fabricated 0 annealed to obtain lower strength temper T1, cooled from an elevated shaping process and naturally aged 1 T4, T4511 solution heat treated and naturally aged 2, 3 T5, cooled from an elevated shaping process and artificially aged T6, T6511 Solution heat treated and artificially aged 2, 3 Note: 1. This designation applies to products which are not cold worked after cooling from an elevated temperature shaping process, or in which the effect of cold work in flattening or straightening has no effect on mechanical properties 2. This designation applies to products which are not cold worked after solution heat-treated, or in which the effect of cold work in flattening or straightening has no effect on mechanical properties 3. This designation applies to products which are not cold worked after solution heat treatment, or in which the effect of cold work in flattening or straightening does not effect mechanical properties Packing: Wooden case or as per requests