Certification:
Description:Key Words: UNS A95083; ISO AlMg4.5Mn; Aluminium 5083-H112; AA5083-H112 Component Wt. % Al 92.4 - 95.6 Cr 0.05 - 0.25 Cu Max 0.1 Fe Max 0.4 Component Wt. % Mg 4 - 4.9 Mn 0.4 - 1 Other, each Max 0.05 Other, total Max 0.15 Component Wt. % Si Max 0.4 Ti Max 0.15 Zn Max 0.25 Mechanical Properties Hardness, Brinell 81 81 500 kg load with 10 mm ball. Calculated value. Hardness, Knoop 104 104 Converted from Brinell Hardness Value Hardness, Rockwell B 50 50 Converted from Brinell Hardness Value Hardness, Vickers 91 91 Converted from Brinell Hardness Value Tensile Strength, Ultimate 300 MPa 43500 psi Tensile Strength, Yield 190 MPa 27600 psi Elongation at Break 16 % 16 % In 5 cm; Sample 1.6 mm thick Modulus of Elasticity 70.3 GPa 10200 ksi In Tension Compressive Modulus 71.7 GPa 10400 ksi Poisson's Ratio 0.33 0.33 Estimated from trends in similar Al alloys. Shear Modulus 26.4 GPa 3830 ksi Shear Strength 180 MPa 26100 psi Calculated