8.5 mm Aluminum Tent Pole Low Plasticity With Mill Finish Surface
 

1) Alloy: 7001,7075,etc

2) Temper: T6

3) Specification:

8.0*0.7mm    9.5*0.7mm        9.5*0.4 mm  11*0.8mm    11*1mm   8.5*0.7mm     7.9*0.7mm   8.5*0.75mm etc accoring clients request

4) Surface: mill finish, anodized and colored etc.

5)color: white, yellow, red, purple ,blue, black, Camouflage ,assorted colors etc

6) Delivery time: approx 20-30 days after confirming order.

6) Minimum order quantity: several kgs per size

7) The term of payment: T/T,LC

8) Packing: Export standard, wooden box packing or according clients request .

9).Feature: high strength alloy, Aluminum alloy tents, can reduce weight tent, and improve the performance of tents.

10)Supply ability:1000ton/month

11)suit for :1 people,2people,3-4 people,5-8 people

7001/7075 etc aluminum pipe production technology 

1.Aluminum bar through the peeling after punch 1200 t extruder extrusion forming Ø and x 2.0

2.Large diameter through the cold machine after cold drawn, with fire degradation process to the necessary 

3.specifications, is commonly Ø 8.5 x 0.72 ~ Ø 7.9 x 0.72 MM

4.Aluminum tube forming later, straightening machine straightening, cutting machine cut to size

5.Chamfering process, is the place where the cut hair cut into smooth

6.Surface oxidation color for the core assembly, cut loose fire

7.Assembly product

7075 aluminum is a cold treatment forging alloy, high strength, and far better than mild steel.

7075 aluminum tube is one of the most powerful alloy in business. Common corrosion resistance,good mechanical capacity and anodic reaction. Fine grain can make the deep drilling performance even better, tool abrasion resistance increase, and thread rolling is more different.

7075 aluminum chemical component
 Si :0.40

 Cu :1.2～2.0
 Mg:2.1～2.9
 Zn:5.1～6.1
 Mn:≤0.30
 Ti :≤0.20

 Cr:0.18～0.28
 Fe: 0.50
 remark: single:≤0.05 ;total:≤0.15
 Al: the rest

7075 aluminum tube processing features

7075 aluminum is called a super-high strength aluminum alloy, the yield strength of alloy is close to tensile strength. Yield strength and intensity is relatively high .But low plasticity and high-temperature strength,it should be used for bearing structure at room temperature and below 120℃.The alloy is easy to be processed, having better corrosion resistance and higher toughness. It is widely used in aviation and aerospace field, and become one of the most important structural materials in this field.  

Physical property and mechanical capacity 　

1.tensile strength:524Mpa
2.0.2% yield strength 455Mpa
3.elongation: 11%
4.elasticity modulus:E⁄Gpa:71
 

7075 aluminum tube product feature
1.high strength and heat-treatable alloy.
2. good mechanical capacity
3. good workability
4. easy processing, good abrasion resistance.
5. good corrosion resistance and oxidation resistance.

welcome contact us with details .