Delivery Time:10-15Days after the 30%payment
Certification:ISO9001，UKAS，SGS

Quick Detail:

Place of origin: China (Mainland)

Brand name:Adv-ti

Material:titanium

Standard: ASTM B265,AMS4911, AMS4916

Technique:hot rolled

Application:heat exchanger

Grade:GR1 GR2 GR5

thickness:0.1-10mm

length:2000-8000mm

processing technique:titanium sponge —compacting electrode—melting—titanium ingots—forging—slab—hot rolling—hot-rolled sheets

Advantage:

  Excellent corrosion resistance

strong oxidation resistance

 long life time

non-magnetic

non-poisonous

high and low temperature resistance

small density

High tensile strength

Applications:

With the development of science and technology, the application field of titanium is becoming more and more broad, such as medical, automotive, sports, etc.

Through these application ,its good characteristics is more and more cognized and affirmed ,and integrate into our production applications instead of other metals with the fastest speed , even in our body.

Mechanical properties of titanium plate

(1)mechanical property at room temperature

Trade mark	Thickness(mm)	properties at room temperature,(no less than)
Tensile Strength   σbMPa	yield strength   σ0.2MPa	elongation δ5%	Bending angle α degree(no less than)
GR1	0.3～10.0	370-530	250	45-30	140-130
GR2	0.3～110.0	440～620	320	25	100-80
GR5	0.8～10.0	895	830	12-10	35-30

 (2)Titanium plate temperature mechanical properties

Trade mark	Test temperature ℃	properties at high temperature,(no less than)
Tensile Strength σbMPa	Endurance strength σ100hMPa
GR5	400	600	550
500	450	200

surface  quality:

1 The surface of the titanium plate should be smooth with its metal colour. The plate was permited to sand blasting with surface before delivery.

 2 The surface was allowed with light darkness and water print in part ；local defects ,scratch,indentation and scallops with thickness less than half of the thickness was allowed ,but the minimum thickness should be ensured.

 3 There should not be macro defects such as crack,peeling, oxide skin,backfin,and mixture with metal and non-metal.also should not be alkali washed too much.

 4The plate was allowed to clear away the local defects along the direction of rolling ,but the thickness after clearness should not less than the minimum thickness allowed.

5In addition, the plate should not be delamination.