Nickel 200 / UNS N02200 / 2.4060 Nickel Alloy Strip ASTM B162
1. Grade: Nickel 200
2. Process: VIR - VAR - ESR - Forging - Cold Rolling - Semifinished - Finished
3. Delivery Condition: Cold rolled
4. Surface Condition: 2B
5. Thickness: 0.01-6.35mm
6. Length*Width: Custom design
6. Specification: ASTM, ASME, GB, JIS, GOST, DIN, etc.
7. Packing: Plywood case, Bundle
General Introduction
|
Grade |
Ni200 (Purity>99.9%), Ni201 (99.5%) |
|
Condition |
Hard (Y) /Soft (M)/Half Hard (Y2) |
|
Dimension |
Thickness 0.01-6.35mm |
|
Width 2-650mm |
|
|
Length min. 500mm |
|
|
Standard |
ASTM B162 |
Properties
|
Density |
Melting point |
Coefficient of expansion |
Modulus of rigidity |
Modulus of elasticity |
Electrical resistivity |
|
|
Ni200 |
8.9g/cm3 |
1446°C |
13.3 µm/m °C (20-100°C) |
81kN/mm2 |
204kN/mm2 |
9.6μW• cm |
|
Ni201 |
1446°C |
13.1µm/m °C(20-100°C) |
82kN/mm2 |
207kN/mm2 |
8.5μW• cm |
Chemical Composition
|
Grade |
Element Composition/% |
|||||||
|
Ni+Co |
Mn |
Cu |
Fe |
C |
Si |
Cr |
S |
|
|
Ni201 |
≥99.0 |
≤0.35 |
≤0.25 |
≤0.30 |
≤0.02 |
≤0.3 |
≤0.2 |
≤0.01 |
|
Ni200 |
≥99.0 |
≤0.35 |
≤0.25 |
≤0.30 |
≤0.15 |
≤0.3 |
≤0.2 |
≤0.01 |
Applications
Manufacture and handling of sodium hydroxide, particularly at temperature above 300C. Production of viscose rayon. Manufacture of soap. Analine hydrochloride production and in the chlorination of aliphatic hydrocarbons such as benzene, methane and ethane. Manufacture of vinyl chloride monomer. Reactors and vessels in which fluorine is generated and reacted with hydrocarbons.