Monel 400 / UNS N04400 / 2.4360 Nickel Alloy Forged Ring ASTM B564
1. Grade: Monel 400
2. Process: VIR - VAR - ESR - Forging - Machining
3. Delivery Condition: Forged, Solution Annealed, Aged
4. Surface Condition: Black, Machining
5. OD: Max. 1000mm
6. Specification: ASTM, ASME, GB, JIS, GOST, DIN, etc.
7. Packing: Plywood case
Monel 400 Chemical composition
Alloy | % | Ni | Cu | Fe | C | Mn | Si | S |
Monel400 | Min. | 63 | 28 | | | | | |
Max. | | 34 | 2.5 | 0.3 | 2 | 0.5 | 0.024 |
Monel 400 Physical properties
Density | 8.83 g/cm³ |
Melting point | 1300-1390 ℃ |
Monel 400 Alloy minimum mechanical properties in the room temperature
Alloy state | Tensile strength Rm N/mm² | Yield strength R P0. 2N/mm² | Elongation A 5 % |
Monel400 | 480 | 170 | 35 |
Characteristic as below
Monel 400 is an extremely combination property that use for largest amount and most widely corrosion resistance alloy. This alloy in the hydrofluoric acid and fluoride gas medium with excellent corrosion resistance, as well as to the hot concentrated alkali. At the same time, is also corrosion resistant to neutral solution, sea water, air, organic compounds. An important feature of this is generally do not generate a stress corrosion cracking, good cutting performance.
Monel 400 Metallurgical structure
Monel 400 alloy is high-intensity single-phase solid solution.
Monel 400 Corrosion resistance
Monel 400 alloy in the fluoride gas, hydrochloric acid, sulfuric acid, hydrofluoric acid and their derivatives have a very good corrosion resistance property, and possess better corrosion resistance more than the copper alloy in the sea water. Acid medium: Monel 400 have corrosion resistance in less than 85% consistency of sulfuric acid. Monel 400 is an important material that resistant to hydrofluoric acid. Water corrosion: Monel 400 alloy in most corrosion cases of water, not only excellent corrosion resistance, but also less pitting, stress corrosion, the corrosion rate less than 0.025mm / a. High temperature corrosion: Monel 400 for the work of the highest temperature at about 600 ℃ in general in the air, in the high temperature steam, the corrosion rate less than 0.026mm / a. Ammonia: Monel 400 can be resistant to an hydrous ammonia and aminate conditions corrosion below 585 ℃ due to the high nickel.
Monel 400 Application field
Seamless water pipe in the power factory Sea-water exchanger and evaporator Sulfuric acid and hydrochloric acid environment Crude distillation Sea-water in the use of equipment and propeller shaft Nuclear industry and used in the manufacture of uranium enrichment isotope separation equipment Manufacturing hydrochloric acid equipment used in the production of pump and valve