Delivery Time:25-30 days after advance payment

PLC Controlling 150KG Electric Casting Furnace Plans 0.15 Capacity 380V 300kw h/t

Specifications:

These equipments are suitable for copper and copper alloy melting and casting.

Type	Content(t)	Ele. Capacity(KW)	Voltage(V)	Temperature(° C)	Melting Rate(t/h)
G/T-0.15-45	0.15	45	380	1200	0.15
G/T-0.3-75	0.3	75	380	1200	0.3
G/T-0.5-120	0.5	120	380	1200	0.5
G/T-0.75-185	0.75	185	380	1200	0.75
G/T-1-240	1	240	380	1200	1
G/T-1.5-400	1.5	400	380	1200	1.5
G/T-2-500	2	500	380	1200	2
G/T-3-700	3	700	380	1200	3
G/T-5-1500	5	1500	380	1200	5
Note: For brass, the Ele. Capacity will be 0.85 of the figure; Temperature: 1250 ° C

Description:

1. Minimum Capacity (T): 0.15

2. Melting Furnace Rated Capacity (T):0.8 

3. Holding Furnace Rated Capacity (T): 1.5

4. Rated Voltage (V): 380

5. Phase Number: 3

6. Frequency of Input Current (HZ): 50

7. Melting Rate ( t/h): 0.2

8. Power Consumption(kw h/t) : 300 

9. Temperature Holding Power (kw): 30

10. Rated Power (kw): 60

11. Rating Working Temperature (℃): 1250

12. Cooling Water Pressure (Mpa): 0.2-0.4

13. Cooling Water Consumption (t/h): 1.6 (Coil water jacket)

14. Weight of Iron Core (kg): 221

15. Weight of Molten Hook (kg): 45

Product Introduction: 

The born and development of Melting Furnace for copper rod casting system that break the traditional copper and copper alloy producing way shorten the copper processing time. The traditional process is divided three steps of melting and casting, heating process and cooling process

Advantages: 

i) Stable product quality;

ii) Low energy consumption;

iii) Removable inductor maintain easily; 

iv) PLC controlling, and servo motor driven system;