Ceramic Fiber Module is made of blanket fan folded, or pre-cut blanket stack bonded to form a module, to form a module with cut edges exposed.
► Characteristic:
♦ Low density and low thermal conductivity
♦ To be secured by concealed anchor
♦ Greater mechanical strength
♦ Shorter heat up and cool down time
♦ Resilience and resistance to thermal shock
♦ Flexible and easy to cut or install
♦ Asbestos free
► Application:
♦ High gas flow velocity furnace or duct lining
♦ Direct exposure to heat as furnace hot face lining
| 1260 Saber block | 1400 Saber block | 1260 Uniblock | 1400 Uniblock | |
| Classification temperature (°C) | 1260 | 1400 | 1260 | 1400 |
| Density （ Kg/m3） | 160 ， 192 , 210 | |||
| Linear shrinkage (%) | （1100℃x 24 hrs）1.0 | (1200 ℃x 24 hrs) 1.0 | （ 1100 ℃ x 24 hrs ） 1.0 | (1200℃ x 24 hrs) 1.0 |
| Thermal conductivity Kcal/mh °C (W/mK) ,ASTM C201 (160 kg/m3) | ||||
| mean 400 °C | 0.09 | 0.09 | ||
| mean 600 °C | 0.14 | 0.14 | 0.14 | 0.14 |
| mean 800 °C | 0.21 | 0.21 | 0.20 | 0.20 |
| mean1000 °C | 0.26 | 0.28 | ||
| Available size（ mm/pc ） | 300*300*150 ， 200 ， 250 ， 300 | |||
| 1260 Unifelt | 1400 Unifelt | 1500 Unifelt | 1600 Unifelt | |
| Classification temperature (°C) | 1260 | 1400 | 1500 | 1600 |
| Density （ Kg/m3） | 128 ， 160 | |||
| Linear shrinkage (%) | （ 900°C x 24 hrs ） 1.3 | (1200°C x 24 hrs) 1.5 | （ 1300°C x 24 hrs ） 1.2 | (1400°C x 24 hrs) 1.1 |
| Thermal conductivity Kcal/mh °C (W/mK) ,ASTM C201 (160 kg/m3) | ||||
| 130 kg/m3 | 160 kg/m3 | 160 kg/m3 | 130 kg/m3 | |
| mean 400 °C | 0.12 | |||
| mean 600 °C | 0.17 | 0. 14 | 0.13 | 0.14 |
| mean 800 °C | 0.25 | 0.2 | 0.17 | 0.21 |
| mean1000 °C | 0.28 | 0.24 | 0.27 | |
| Available size（ mm/pc ） | 300*300*50 ， 75 |