Ferro Silicon Barium Calcium Powder Inocuant deoxidizer for smelt, FeSiBa Alloy

Specifications:

Model No.	Chemical Composition %
Si	Ba	Ca	Al	Fe
BN-A1	70-75	0.8-1.5	1.0-2.0	≤2.0	Balance
BN-A2	68-75	1.2-2.4	1.0-2.0	≤1.0	Balance
BN-B1	70-75	3.0-5.0	1.0-2.0	≤2.0	Balance
BN-B2	70-75	4.0-6.0	1.5-2.5	≤1.0	Balance
BN-C1	70-75	2.0-3.0	1.0-2.0	≤2.0	Balance
BN-C2	45-52	2.0-4.0	-	≤1.0	Balance

Maximum spheroidization.Encourage type A flake graphite formation in gray irons. maxmum chill reduction. Reduced relative hardness to improve machinability. Reduced fading tendency. reduced sectional sensitivity. Stable chemical composition. Low melting point(~1300) for easy absorption.

Applications:

The production practice indicated that it was available to decrease acid soluble aluminium content in alloy constructional steel and spring steel and increase surface quality of products and reduce reject amount of bearing steel products because of D type inclusion by using barium silicon alloy deoxidizer partially to replace aluminium.

Same as other Si base inocuant. 0.1-0.5mm is for late stream inoculation. Addition rare is about 40% of FeSi75.

Competitive Advantage:

Unique composition of special inoculant is welcomed and it can be made and sipplied at convenience.

Supplied in the form of grains or following special requirement. Packed plastic braids with inner wetresistant plastic film. Per packed parcel is 25kg n.w.