SS400 Structural Steel

JIS G 3101 SS400 is one of the most commonly used hot rolled general structural steel. 

Supplied as plates, sheets, flats, bars, sections etc. 

They are cheap, excelling in weldability & machinability. 

SS400 Mechanical Properties

Density (kg/m3) 7860 Young’s Modulus (GPa) 190-210 

Tensile Strength (MPa) 400 – 510 MPa 

Yield Strength (MPa) 205-245 MPa Poisson's ratio 0.26 

SS400 Hardness

Brinell hardness (HB) 160 

SS400 Equivalents

DIN Equivalents for JIS SS400

DIN 17100 St37-2, St 44-2 

ASTM Equivalents for JIS SS400

ASTM A36, ASTM A283 Grade C,D 

EN Equivalents for JIS SS400

EN S235, S275

BS 40A, 43A 

GB/T Equivalents for JIS SS400

GB/T Q235B, Q275B

SS400 Chemical Composition

As per JIS G 3101, Carbon (C), Silicon (Si) and 

Manganese (Mn) content are not controlled.

 Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels. 

Melting Point

Melting point of SS400 is 1430 Degree Celsius.