Product Name:Excellent Physical Strength Injection Molded Magnet With High Magnetic 
 
Each finished good is unique in size,shape,magnetic and mechanical properties.
 
 
Listing Description
 
1. Complex shapes with high precision.
2. Adjustable magnetic properties.
3. Insert molding.
 
 
Applications
 
 
Sensors,Linear actuators,Microphone assemblies, Magnetic separators,DC and servo motors,
Speakers Printers,Magnetic hooks,Computer rigid disc drives,Beam controls,Intelligent toys,
MRI/NMR Electric component,etc.
 
 
Injection molded NdFeB
 
 
Besides sintered magnets and bonded magnets categories, injection molded magnet is one of the 
more important developments in magnetic materials, it has opened a new world of application 
opportunities. Similar to plastic injection molding, magnet injection molding process is by mixing the 
magnetic powder together with polymer binder, heated in the injection machine and shooting the 
melted mixtures into the mold to achieve different shapes of products.
 
 
Injection Molded NdFeB Features
 
1.  Injection molded magnets can be of very complex shapes with high precision, typically, tolerance 
is0.005mm, it is suitable for high precision parts.
2. It is a new technology to achieve adjustable magnetic properties, composite molding, elastic 
magnetization and high mechanical strength.
3. By doing insert molding, magnetic material can be directly molded into or onto other assembly 
components without further assembly process.
4. Magnetic powder is neodymium-iron
boron (NdFeB), either isotropic or anisotropic. And Polymer binders utilized are PA6,PA12 and PPS.
 
5. Anisotropic NdFeB powder achieves the highest magnetic force as injection molded magnet. 
And it is possible to achieve BHmax 17GMOe, and can replace some of sintered products.
 
 
Injection NdFeB Material Magnetic Properties
 
Maximum application temperature is related with magnetic powder and polymer binder. NdFeB material 
suffers significant irreversible magnetic loss above 120°C, regardless of which binder is used. And on 
the other hand, the HDT (heat deformation temperature) of the binders is low, when application 
temperature exceeds the HDT, the binder in injection molded magnet will become soft at some extent, 
which jeopardizes the product. Maximum application temperatures are listed in following sheet.
 

NdFeB Material Magnetic Properties
Grade	Material	Magnetic feature	Residual flux density  (Br)	Coercive force                      (bHc)	Intrinsic Coercive force (iHc)	Max Energy Product (Bhmax)	Max application Temperature
mT	Gs	KA/m	Oe	KA/m	Oe	KJ/m 3	GMOe	Centigrade
MJMN1210	NdFeB+PA12	Isotropic	454	4,540	305	3,830	691	8,680	35.0	4.40	100
MJMN1220	NdFeB+PA12	Isotropic	507	5,070	338	4,250	693	9,048	43.0	5.40	100
MJMN1230	NdFeB+PA12	Isotropic	536	5,360	353	4,430	773	9,700	47.0	5.90	100
MJMN1240	NdFeB+PA12	Isotropic	619	6,190	385	4,840	704	8,850	59.7	7.50	100
MJMN1310	NdFeB+PA12	Anisotropic	683	6,830	484	6,075	1,154	14,495	86.2	10.80	100
MJMN1320	NdFeB+PA12	Anisotropic	735	7,350	515	6,470	1,136