Stainless steel shot is kind of abrasive used for shot blasting machine, shot blasting equipment, shot peening machine, shot peening equipment, sandblasting machine, sandblasting equipments, steel material pretreatment production line, steel plate pretreatment production line, steel structure pretreatment production line.
Types:0.2~2.5mm

Chemical Composition:

304 Austenite Type:C<0.25%   Cr=16~18%  Ni=6~10%   Si<1%  Mn<2%

430 Ferrite Type:   C<0.25%  Cr=16~18%   Si<1%   Mn<1%

410 Martensite Type:C<0.25%   Cr=11~13%  Si<1%   Mn<1% (

Note: other chemical components can be provided.)

Micro Hardness:308~509HV(Vickers) 32~50HRC (Rockwell)

Durability: 6500 times

Microstructure:304 type: Deformed Austenite

               430type: Deformed Ferrit

               410type: Deformed Martensite

Density:   7.8g/cm3

Stainless steel cut wire shot is ideal shot blasting and shot peening metal material which is also called stainless steel cut wire shot abrasive, stainless steel shot, blasting abrasive, shot blasting abrasive, blasting material, shot blasting scale-removal abrasive, peening abrasive, grit peening abrasive, grit peening machine abrasive, shot peening scale-removal abrasive, shot peening material, grit peening material, grit peening consumable, scale-removal abrasive, steel plate preparation abrasive, steel preparation abrasive. 
Types:0.3~2.5mm

Chemical Composition:

304 Austenite Type:C<0.25%   Cr=16~18%  Ni=6~10%   Si<1%  Mn<2%

430 Ferrite Type:   C<0.25%  Cr=16~18%   Si<1%   Mn<1%

410 Martensite Type:C<0.25%   Cr=11~13%  Si<1%   Mn<1% (

Note: other chemical components can be provided.)

Micro Hardness:308~509HV(Vickers)32~50HRC (Rockwell)

Durability: 7000 times

Microstructure:304 type: Deformed Austenite

               430type: Deformed Ferrit

               410type: Deformed Martensite

Density:   7.8g/cm3