Hot Sale Large Cr-Mo Alloy Steel Liners , SAG Mills Liners

Quick Details

1. The Large Cr-Mo Alloy Steel Liners up to 2tons are designed for higher reliability in AG mills and  

  SAG mills.

2. Hardness: HRC33-43.

2 tons Shell Liners for SAG Mills  

1. Hardness difference from surface to center is less than HRc2.

2. The Large Cr-Mo Alloy Steel Liners up to 2tons are widely used for AG mills, SAG mills, large ball mills.

3. The steel liners have higher reliability in AG mills and SAG mills.

4. Impact value:AK≥10J.

5. Hardness: HRC33-43.

In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.

Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

Chemical Composition & Mechanical Property of Wear-resistant Castings

Item	Cr-Mo Alloy Steel I	Cr-Mo Alloy Steel II	Cr-Mo Alloy Steel III	High Cr white iron	High Cr Alloy Steel	High Manganese Steel	Ni-Hard cast iron
C	0.30~0.50	0.65~0.90	0.40~0.90	2.40~3.20	1.1~2.2	0.90~1.30	2.40~3.60
Si	0.50~1.20	≤0.75	0.70~1.20	0.60~1.20	0.60~1.20	≤0.08	≤0.80
Mn	0.40~1.20	0.50~1.20	0.60~1.00	0.50~1.00	0.50~1.00	11.00~18.00	≤2.0
Cr	1.70~2.50	1.50~2.50	4.00~7.00	12.00~30.00	11.00~30.00	1.50~2.50	1.5~10
S	≤0.04	≤0.06	≤0.04	≤0.04	≤0.04	≤0.04	≤0.15
P	≤0.04	≤0.06	≤0.06	≤0.06	≤0.06	≤0.06	≤0.15
Mo	≤0.5	≤0.5	≤0.5	0.10~3.0	0.10~3.0	≤1.0	≤0.10
Cu	0.10~0.60	≤0.25	0.20~0.40	0.10~1.00	0.10~1.00	-	-
Ni	≤0.50	≤0.30	0~0.30	0~0.30	0~0.30	-	3.3~10
Re	≤0.02	≤0.02	≤0.02	-	-	-	-
Equivalent Specifications	DL/T 681-1999 GB/T26651-2011	AS 2074 L2B Mod	DL/T 681-1999	GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401.	GB/T 5680-1998