High Abrasion Cr White Iron End Liners For Cement Mill Linners
USD $ 1950 - $3200 /
Min.Order:1
Wear Steel Mill Liners For Hoppers Hardness More Than HRc48 DF055
Cr-Mo Alloy Steel Grates For Cement Mill Liners , Wear Resistant Castings
Alloy Steel Dimensions Steel Mill Liners Application Cement Mill DF087
High Manganese Steel Stepped Liners With High Cr For Cement Mill
HRC65 High Cr Steel Blind Cement Mill Liners Plates With Ni-Hard Cast Iron
High Abrasion Cr White Iron End Liners For Cement Mill Linners
Quick Details
High Cr Casting liners Feature:
1.The series are designed for high abrasion performance.
2.HRC52-65, AK5-15J.
3.The materials conform to GB/T 8263-1999.
High Cr Casting liners Description:
A. The series are designed for high abrasion performance.
B. The antiwear property is four times as much as that of high manganese steel
and twice of low alloy steel.
C. HRC52-65, AK5-15J.
The materials
The materials conform to GB/T 8263-1999,
BS 4844 3E,
AS 2027 CrMo 15/3,
AS 2027 CrMo 20/2/1,
AS 2027 Cr27,
ASTM A532 Class III type A 25% Cr,
ASTM A532Class II type B 15% Cr-Mo.
China cement mill liners supplier provides cement mills liners services to worldwide casting liners customer. Hope you find our cast liners for cement mills process and cement mill liner product description helpful.
In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0.10~1.00 |
0.10~1.00 |
- |
- |
Ni |
≤0.50 |
≤0.30 |
0~0.30 |
0~0.30 |
0~0.30 |
- |
3.3~10 |
Re |
≤0.02 |
≤0.02 |
≤0.02 |
- |
- |
- |
- |
Equivalent Specifications |
DL/T 681-1999 GB/T26651-2011 |
AS 2074 L2B Mod |