SUS630 / 17-4PH / 05Cr17Ni4Cu4Nb Stainless Steel / Stainless Sheet

1.  Grade:SUS630/17-4PH/05Cr17Ni4Cu4Nb stainless steel 

2. Technology:Hot rolled, ESR , ANNEALING or Solution

3.  Mill Name:Changgang

4.  MOQ:5 Tons

5.  Payment term:30% deposit. the balance against L/C at sight or T/T

6.  Packing term:Waterproof paper + wood pallet or as per customers\' requirements

7. Supply Ability:100Ton/Month

8. Chemical composition:

C	Si	Mn	P	S	Cr	Ni	Cu	Nb
≤0.07	≤1.00	≤1.00	≤0.030	≤0.035	15.50-17.50	3.00-5.00	3.00-5.00	0.15~0.45

9. Physical properties

   Tensile strength: σb (MPa):480℃,≥1310; 550℃,≥1060;  

                        580℃,≥1000; 620℃,≥930

   Conditions yield strength: σ0.2 (MPa):480℃,≥1180;

                            550℃,≥1000;580℃,≥865;620℃,≥725

   Elongation rate: δ5 (%):480℃,≥10;550℃,≥12;

                                580℃,≥13;620℃,≥16

   Reduction of Area: ψ (%):480℃,≥40;550℃,≥45;

                                   580℃,≥45;620℃,≥50

   Hardness: Solid solution, ≤363HB and ≤38HRC;

               480℃, ≥375HB and ≥40HRC; 

               550℃, ≥331HB and ≥35HRC; 

               580℃, ≥302HB and ≥31HRC; 

               620℃, ≥277HB and ≥28HRC 

10. Heat Treatment Process: Solid solution 1020～1060℃ Rapid 

     cooling; 480℃,After solution treatment,470～490 Air-cooled; 

     550℃,After solution treatment,540～560℃ Air-cooled; 

     580℃,After solution treatment,570～590℃ Air-cooled; 

     620℃,After solution treatmen,610～630℃ Air-cooled. 

11. Metallurgical structure:The organization is characterized  precipitation hardening.

12. Specifications:

Stainless steel plate(mm)	Brand
Thickness	Width	Length
5~65	610	3000~6000	Panggang

13. Applications:     

  · Offshore platforms, helicopter deck, other platforms

  · Food Industry

  · Pulp and paper industry

  · Aerospace (turbine blades)

  · Mechanical components

  · Nuclear waste barrel

14. Competitive Advantage:

l High strength

l High hardness 

l Good weldability

l Corrosion resistance performance

l Low carbon content, 0.05%

l Heat treatment is simple, good machinability

l State-owned manufacturer of quality assurance

l Faster production , delivery time just only 30 to 35 days

l All materials are quality tested three times, in order to meet the high standards of customer