Stainless steel 304(CF8) clamp precision investment casting by lost wax process from ISO certificated foundry.

Quick Detail:
 

Precision investment casting technology for stainless steel clamp of pipe fitting industry ; Casting type: silica sol lost wax process; PED/AD2000 certificated; ISO9001:2008 certificated; Chemical composition tested by German spectrometer; Physical property inspection report available.

 
 
Description:
 

Stainless steel, carbon steel, Nickel-based alloy steel investment castings with maximum size 500*500*350mm; ASTM,JIS,DIN,BS,MIL Standards.

Stainless Steel (70%)	Carbon Steel	Alloy Steel
303,  430, 420, CF3M (AISI 316L), CF8M (AISI 316), CF8 (AISI 304),CD4MCu, CD4MCuN,ANC20,1.4408,1.4517, 1.4306, 17-4PH, SCS1 and more	1020, 1040, S355JR, SCS16, SCS14, SCS13, 1.0619, WCB, 1045 , LCC and more	ANC2,CLA12C,42CrMo,8Q,4140,6150 and more

Investment Casting Process:

1.TOOL MAKING

A wax injection mold is designed and built to produce castings per customer specifications.

2. WAX PRODUCTION

A wax pattern is produced from the wax injection mold.

3. PATTERN ASSEMBLY

Wax patterns are attached to gating system by hot knife.

4. SHELL MAKING

The pattern assembly is dipped into a ceramic slurry, coated with a refractory material and dried. The process is repeated until the desired thickness and strength is achieved.

5. DEWAXING

Using regulated steam pressure, an autoclave melts and remove the wax from the ceramic shells.

6.SHELL PREHEAT

High temperature ovens cure and preheat the ceramic shells before pouring.

7. CASTING

Pre-heated Ceramic cavities are poured with the molten metal.

8.KNOCK OUT

The ceramic shell is removed by vibration knocking and the cluster is cleaned.

9.CUT OFF

Castings are cut off from the gating system.

10.MACHINING,SURFACE FINISH,AND INSPECTION

After cut off and gate removal, all secondary finishing operations are performed. Each casting is inspected according to customer specifications and requirements.

 
 
Applications:

 
Pumps
Valves
Pipe Fittings
Automotive
Marine and Oil
Machinery
Power & Energy
Other Mechanical Castings
 

 
Specifications:

Casting process type	silica sol lost wax casting
Maximum Casting Size	500*500*350mm
Casting weight	10g~80kg
Wall thickness	1.5-2mm Min
Standards	ASTM,JIS,DIN,BS,MIL
Machining	CNC machining, CNC lathe
Surface finish types	electro polishing, satin finish, hand polishing, pickled, zinc plating, vibration polishing;
Tolerances Standard	VDG P690
NDT test service	Dye test, X ray test etc

 
Competitive Advantage:

Investment Casting is generally more expensive than it\'s associated metal casting methods of \"die casting\" or \"sand casting\", but can produce complicated shapes that require little rework or machining. Investment casting is used in many advanced technical industries such as Aerospace, Power Generation, Oil & Gas, Military & Defence, Medical, Commercial and Automotive.