Wearable Abrade-resist Aluminum Oxide Ceramic Brick, Bending Strength 290MPa
Negotiable /Set
Min.Order:1 Set
Yixing Feifan Ceramics Co.,Ltd
Corrosion Resistant ROHS Hardness 85 Mechanical Aluminum Oxide Ceramic Sealing Ring
Custom Made Industrial High Purity White Al2O3 / Alumina Ceramic Grinding Wheel
Light Weight Heat-Resistant Big Hardness White 96% Aluminum Oxide Ceramic Plate
CIP Forming, High Voltage Resistant 95%, 99%, 99.7% Aluminum Oxide / Alumina Ceramic Box
High Pure Aluminum Oxide / Al2O3 / Alumina Ceramic Plunger, Bending Strength 290MPa
95% AL2O3 Metalized Aluminum Oxide Ceramic Ring With Ra 0.4 / Sim Ra 0.8 Surface finish
Wearable Abrade-resist Aluminum Oxide Ceramic Brick, Bending Strength ≥ 290MPa
Description:
Wearable ceramic is the special corundum ceramic that been sintered under 1700℃ with the main raw material of Al2O3 and flux of rare metal oxide. Using the high strength organic/inorganic bond to felt together, and then grinding to the size as drawing required.
Performance:
1. Big hardness, the ROHS hardness is HRA80-90, just inferior to diamond, the wearable ability is much better than the wearable steel and stainless steel
2. Wearable ability is excellent. Equal to 266 times of manganese steel, 171.5 times of high chrome cast-iron. Under the same working condition, can extend the equipment working life at least above 10 times.
3. Light weight, the bulk density is 3.6g/cm3, only half of steel, can alleviate the equipment burthen greatly.
4. Hard adhesives, good heat-resistant.
Applications:
The enterprises of Electricity,steel,smelt,mechanism,colliery,mine,chemical,cement,oil field ,will choose the different products according to their special requirements for the wearable mechanical instruments that works in the system of coal transfer, material transfer, milling, dust removing, and so on.
Specifications:
Main Technical parameters:
Alumina content≥95%
Bulk Density≥3.6 g/cm3
ROHS Hardness HRA≥85
Compressive Strength≥850 Mpa
Fracture Toughness KΙC ≥4.8MPa•m1/2
Bending strength≥290MPa
Coefficient of thermal conductivity: 16W/m.K