Item

Test condition

Test method

Test data

Unit 

Basic Properties

Melt Floe Rate

190°C/2.16kg

ASTM D-1238

20

g/10min

Density

---

ASTM D-792

0.954

g/cm3

Mechanical Properties

Hardness

---

ASTM D-2240

57

Shore D

2%Secant flexural modulus

---

ASTM D-790 B

167,000(1151)

psi(MPa)

Tensile Strength at Break

---

ASTM D-638

2000(14)

psi(MPa)

Tensile strength at yield

---

ASTM D-638

4100(28)

psi(MPa)

Elongation at break

---

ASTM D-638

250

%

Yield strain

---

ASTM D-638

7

%

Tensile Impact Strength

---

ASTM D-1822,Type S

20(42)

ft?lb/in2(kJ/m2)

Resistance to environmental stress cracking resistance

122?H(50°C),F50,100%lgepal,hrs

ASTM D-1693

3

---

Heat properties

Brittle Temperature

---

ASTM D-746

<-105(<-76)

?H(°C)

Heat Deflection Temperature

66psi(0.45MPa)

ASTM D-648

163(73)

?H(°C)

Vicat Softening Point

---

ASTM D-1525

261(127)

?H(°C)

DSC melt point

---

Dow Method

266(130)

?H(°C)

DSC Crystallization point

---

Dow Method

243(117)

?H(°C)